对硝酸级（NAG）310L不锈钢焊接接头在含氧化性离子的沸腾硝酸中进行浸泡实验及金相分析。研究表明，在不同Cr6+含量的沸腾 40%HNO3中，材料的腐蚀程度主要受Cr6+含量的影响。随Cr6+含量的增加，母材和焊缝均出现不同程度腐蚀，但焊缝较母材腐蚀严重。 Cr6+含量是促进焊缝过钝化腐蚀和晶间腐蚀的主要因素。
orrosion resistance of welding joints of 310L(NAG) stainless steel in boiling nitric acid with different Cr6+ ions contents was investigated. It is shown that Cr6+ ions can remarkably enhance corrosion attack on welding joints, and with intergranular attack in heat affected zone and weld metal. The weld metal was suffered more severely corrosion attack, but in pure boiling nitric acid, welding joints exhibit strong corrosion resistance.
参考文献
| [1] | Decugis J C. Proceedings of a Technical Committee Meeting on Materials Reliability in the Back End of the Nuclear Fuel Cycle [C]．Vienna: International Atomic Energy Agency, 1987: 148-152[2]Shaw R D. Corrosion prevention and control at Sellafield nuclear fuel reprocessing plant [J]. Br. Corros. J., 1990, 25(2): 97-107[3]Yamamoto. Proceedings of a Technical Committee Meeting on Materials Reliability in the Back End of the Nuclear Fuel Cycle [C]．Vienna: International Atomic Energy Agency, 1987：129-146[4]Decours J. Proceedings of a Technical Committee Meeting on Materials Reliability in the Back End of the Nuclear Fuel Cycle [C]．Vienna: International Atomic Energy Agency, 1987：117-126[5]Balakrishnan V P．Proceedings of Workshop on Failure Analysis [C]. Bombay: Corrosion Evaluation and Metallography, 1992：273-282[6]Baldev, Kasiviswanathan. Proceedings of the International Conference on Advance in Mechanical and Industrial Engineering [C]. India: University of Roorkee, 1997：1-10[7]Kamachi．Corrosion study on materials of constructions for spent nuclear fuel in reprocessing plant equipment [J]. J. Nuclear Mater. 1993，20(3)：73-82[8]Lu S Y, Zhang K, Yang C Q, et al. Stainless Steel [M]. Beijing：Atomic Energy Press，1995[9](陆世英，张凯，杨长强等．不锈钢 [M]．北京：原子能出版社，1995)[10]Steel D F．Corrosion control in nuclear fuel reprocessing plants [J]．Atom, 1986，353：5-9[11]Nagano H. Corrosion of stainless steel in strong oxidizing nitric acid [J]. Anticorros. Technol., 1988，37(5)：301-310[12](长野博夫．在强氧化性硝酸中的不锈钢腐蚀 [J].防食技术，1988，37(5)：301-310)[13]~} Kiuchi K．Proceedings of RECOD-91 [R]．London: British Journal of Applied Physics, 1991: 54 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%