采用传统固相反应法制备了Bi2(Mg1/3Nb2/3)2O7(β-BMN)介电陶瓷,借助X射线衍射(XRD)研究了不同预烧温度合成β-BMN粉体的物相组成,借助扫描电镜(SEM)研究了不同烧结温度β-BMN的显微结构,考察了不同烧结温度和保温时间对β-BMN陶瓷性能的影响.结果表明:合成温度为850℃时已经完全形成主晶相(β-BMN).随着烧结温度的增加,样品的介质损耗(tanδ)先变小后增大,而相对介电常数(εr)先增大后减小.当烧结温度为1000℃保温5h时,得到的陶瓷的综合性能较佳:ρ=7.69g/cm3,εr=207,tanδ=0.00197.
参考文献
| [1] | 张玉娟 .微波介质陶瓷与钙钦矿型化合物[J].上海建材学院学报,1995,8(01):59-70. |
| [2] | 何进;杨传仁.微波介质陶瓷材料综述[J].电子元件与材料,1995(04):7-13. |
| [3] | Low-loss, tunable bismuth zinc niobate films deposited by rf magnetron sputtering[J].Applied physics letters,2003(12):2411-2413. |
| [4] | Jiang G S W;Li Y R;Li R G et al.Dielectric properties and tunability of cubic pyro-chlore Bi1.5MgNb1 5O7 thin films[J].Applied Physics Letters,2009,94:162908. |
| [5] | Liu D H;Huang S Q;Yao X .Phase structure and dielectric properties of Bi2O3-ZnO-Nb2O5-based dielectric ceramics[J].Journal of Ameiican Ceramic Society,1993,76(08):2129-2132. |
| [6] | Chen S Y;Lee S Y;Lin Y J .Phase transformation,reaction kinetics and microwave characteristics of Bi2O3-ZnO-Nb2O5 Ceramics[J].Journal of the European Ceramic Society,2003,23(06):873-881. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%