以丙烯酸为接枝单体，二苯甲酮为光敏剂，在紫外光的引发下对废胶粉进行表面接枝，用正交方法对改性工艺进行了优化，制备了改性废胶粉／天然橡胶复合材料，表征了改性前后废胶粉的表面形貌和结构，考察了其加入量对复合材料力学性能的影响。结果表明：当丙烯酸和二苯甲酮与废胶粉的质量比分别为10％和9％，废胶粉粒径为150μm和光照时间为4min时，为最佳工艺条件，此时接枝率最高，达3．38％；接枝改性后的废胶粉表面粗糙度增加；随改性废胶粉含量的增加，复合材料的拉伸强度和邵氏A硬度先增大后降低，并在质量分数10％时达到最大值，分别为27．28MPa和69．2HSA。
The surface of waste rubber powder （WRP） grafted with acrylic acid （APt） was performed under the inducing of ultraviolet （UV） using benzophenone （BP） as photosensitizer. The fabrication parameters were optimized via orthogonal method. The modified WRP/natural rubber （NR） composites were fabricated. The surface morphology and structures of WRP before and after modified, and the effects of WRP content on the mechanical properties of WRP/NR composites were studied. Results show that the highest grafting degree of 3. 38% was gained in the optimized condition with 10wt% AA, 9wt % BP, 150μm grain size of WRP and 4 min of illumination time. The rougher surface of modified WRP was observed when compared with the unmodified samples. The tensile strength and Shore A hardness were increased first, and then decreased with the content of modified WRP increased, and the peak values （27. 28 MPa and 69.2 HSA, respectively） were obtained when 10wt% WRP added.
参考文献
| [1] | 蒋涛,邹国享,程时远.胶粉的活化改性及其在弹性体中的应用研究进展[J].弹性体,2003(02):47-51. |
| [2] | 李俊,刘成果,陈庆民.天然橡胶接枝改性研究进展[J].高分子材料科学与工程,2008(03):24-27. |
| [3] | 王晓,马海涛,李淳,王娜,耿新英.亚麻织物紫外光接枝丙烯酸的改性[J].纺织学报,2010(09):84-88. |
| [4] | 邢晓东,王晓工.聚合物表面紫外光接枝技术及应用进展[J].化工进展,2008(01):50-56,73. |
| [5] | 于志强,顾辉,张志谦,田茂忠.紫外光辐照聚丙烯粉固相接枝及其表征[J].材料科学与工艺,2000(01):16-20. |
| [6] | Shanmugharaj AM;Kim JK;Ryu SH .Modification of rubber surface by UV surface grafting[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(16):5714-5722. |
| [7] | Nakason C;Saiwari S;Kaesaman A .Rheological properties of maleated natural rubber/polypropylene blends with phenolic modified polypropylene and polypropylene-g-maleic anhydride compatibilizers[J].Polymer Testing,2006(3):413-423. |
| [8] | 游长江,李晓勇,谢铌铌,鲁光,冯建中,贾德民.丁苯橡胶/废胶粉弹性体合金的结构与性能[J].高分子材料科学与工程,2006(03):141-144. |
| [9] | 丁国新,程国君,杨小龙,逯全县.废胶粉的表面处理及在天然橡胶中的应用[J].材料科学与工程学报,2011(06):949-953. |
| [10] | 冯予星,王益庆,童亚明,张惠峰,张立群.废胶粉/聚丙烯热塑性弹性体的界面增容研究[J].合成橡胶工业,2003(01):32-36. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%