以TritonX-100/正己醇/正己烷/水为反应介质,采用双微乳液法合成了尖晶石型CoFe2O4磁性纳米颗粒.利用TG-DSC、FTIR、TEM、XRD、VSM等测试技术对CoFe2O4煅烧前后的结构和磁性能进行表征.结果表明,采用微乳液法制备的CoFe2O4前驱物经煅烧后可获得纳米级磁性微粒.煅烧温度对微粒粒径和磁性能有较大影响,经300℃煅烧后的微粒粒径为15nm,700℃煅烧后微粒粒径增大为52nm.样品的饱和磁化强度和剩余磁化强度也随热处理温度的升高而增加.
参考文献
| [1] | Tartaj P;Morales M P;Gonzalez-Carreno T et al.Advance in magnetic nanoparticles for biotechno-logy applications[J].Journal of Magnetism and Magnetic Materials,2005,290:28. |
| [2] | Okuno S N;Hashimoto S;Inomata K .Preferred crystal orientation of cobalt ferrite thin films induced by ion bombardment during deposition[J].Journal of Applied Physics,1992,71(12):5926. |
| [3] | Cornejo DR.;Medina-Boudri A.;Bertorello HR.;Matutes-Aquino J. .Magnetization reversal in co-precipitated cobalt ferrite[J].Journal of Magnetism and Magnetic Materials,2002(1):194-196. |
| [4] | A. Medina-Boudri;D. Bueno-Baques;L. Fuentes-Cobas .Study of reversible and irreversible magnetization processes of coprecipitated cobalt ferrite[J].Journal of Applied Physics,2000(9):6235-6237. |
| [5] | T. A. S. Ferreira;J. C. Waerenborgh;M. H. R. M. Mendonca .Structural and morphological characterization of FeCo_2O_4 and CoFe_2O_4 spinels prepared by a coprecipitation method[J].Solid state sciences,2003(2):383-392. |
| [6] | Kim YI.;Kim D.;Lee CS. .Synthesis and characterization of CoFe2O4 magnetic nanoparticles prepared by temperature-controlled coprecipitation method[J].Physica, B. Condensed Matter,2003(1/4):42-51. |
| [7] | Rondinone A J;Samia A C S;Zhang Z J .Super paramagnetic relaxation and magnetic anisotropy energy distribution in CoFe2O4 spinel ferrite nano-crystallites[J].Journal of Physical Chemistry B,1999,103(33):6876. |
| [8] | Pillai V;Shah D O .Synthesis of high-coercivity cobalt ferrite particles using water-in-oil micro-emulsions[J].Journal of Magnetism and Magnetic Materials,1996,163:243. |
| [9] | Li Yongchang;Park C W .Particle size distribution in the synthesis of nanoparticles using micro-emulsions[J].Langmuir,1999,15(04):952. |
| [10] | Cullity B D.Elements of X-ray diffraction[M].New York:Addison-Wesley,1978:99. |
| [11] | Bate G.Ferromagnetic materials[M].Amaterdam:North-Holland,1980:431. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%