采用液相等离子电解渗氮技术,研究了不同甲酰胺浓度对38CrMoA1钢渗氮层组织及性能的影响.利用OM、SEM、XRD观察分析渗氮层的微观组织结构和物相构成,RF-GDOES和Parstat 2273电化学工作站分别表征渗氮层的元素分布和耐蚀性,并测试分析了渗层截面的显微硬度.结果表明,随着电解液中甲酰胺浓度的升高,渗氮致密层、白亮层、扩散层厚度呈先增加后降低的趋势,渗氮层最大显微硬度值呈增加的趋势;当甲酰胺浓度升高至70%时渗氮层达到最大,为125 μm,白亮层为51 μm;渗氮后扩散层硬度值较高,而心部组织硬度较未处理试样提升约2倍;渗氮层表层主要含Fe2N和Fe3N相,扩散层以Fe16N2、FeN相为主,过渡层主要为α-Fe、FeN0.097相;渗氮层的耐蚀性优于未经处理试样.
参考文献
[1] | 周上祺,侯琼,任勤.38CrMoAl钢离子渗氮微观结构的研究[J].金属热处理,2002(10):10-12. |
[2] | Shigeo Sato;Yuuki Arai;Noboru Yamashita;Atsushi Kojyo;Kenji Kodama;Naofumi Ohtsu;Yukio Okamoto;Kazuaki Wagatsuma .Surface-nitriding treatment of steels using microwave-induced nitrogen plasma at atmospheric pressure[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2012(19):7574-7580. |
[3] | 姚一平.在VDR渗氮炉中进行的真空脉冲渗氮[J].热处理,2008(01):63-65,67. |
[4] | Tarakci M;Korkmaz K;Gencer Y;Usta M .Plasma electrolytic surface carburizing and hardening of pure iron[J].Surface & Coatings Technology,2005(2/3):205-212. |
[5] | 崔国栋,杨川,程海明.38CrMoAl钢气体氧氮共渗处理的组织与性能[J].金属热处理,2008(12):46-48. |
[6] | 周贤良,许武波,华小珍,周浪,崔霞.渗氮时间对38CrMoAl钢液相等离子体渗氮层组织及性能影响[J].材料热处理学报,2014(8):176-181. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%