研究了温度对P(St-co-BA)/P(BA-co-MMA)核壳型复合胶乳的成膜及其性能的影响.通过涂膜干燥速率由线、透光率、吸水率及水蒸汽渗透系数随温度的变化,发现在40℃～90℃内适宜的温度下,可加速膜的形成、提高涂膜的性能.而当在临界温度(90℃)以上成膜或退火时,可使胶膜产生二次相分离,且在膜内产生微裂纹、针孔及空穴等缺陷,但这些针孔不是贯通的.
参考文献
| [1] | Okubo M;Yamada A;Matsumoto .[J].Journal of Polymer Science,1980,203(06):3219－3220. |
| [2] | 刘杰凤,李春海,王志辉,车伟林.核/壳型苯乙烯-丙烯酸酯乳液的研制[J].涂料工业,2003(05):5-8. |
| [3] | 甘孟瑜,刘娟,杨治国.核壳结构丙烯酸酯乳液的合成及性能研究[J].涂料工业,2005(06):5-8. |
| [4] | Schuler B.;Kirsch S.;Pfau A.;Sandor M.;Zosel A.;Baumstark R. .Structure and properties of multiphase particles and their impact on the performance of architectural coatings[J].Progress in Organic Coatings: An International Review Journal,2000(1/4):139-150. |
| [5] | 袁显永;霍东霞;王红英.材料科学与工程[M].北京:原子能出版社,2005:427－430. |
| [6] | Mulvihill J.;Dewilde M.;Toussaint A. .ONSET, FOLLOW UP AND ASSESSMENT OF COALESCENCE [Review][J].Progress in Organic Coatings: An International Review Journal,1997(3):127-139. |
| [7] | Huijs F. .Morphology and film formation of poly(butyl methacrylate)-polypyrrole core-shell latex particles[J].Colloid and polymer science,2000(8):746-756. |
| [8] | Patel A A;Feng J;Winnik M A .[J].Polymer,1996,37(25):5577－5582. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%