采用传统的固相反应法在较低的烧结温度与较短的煅烧时间下制备了(La1.85Sr0.15CuO4)1-x(La2/3 Sr1/3MnO3)x(简写为LSCO/LSMO)超导/铁磁复合材料.结果显示:复合后LSMO中的结构没有发生明显改变,随着温度的降低,所有的复合材料在38 K左右均会出现电阻急剧下降,最终呈现超导现象.甚至当LSMO铁磁性材料掺入达到O.20mol时,复合材料仍旧呈现超导态.同时所有复合样品的超导转变温度TC随着x的增加呈现线性下降的趋势.因此,通过低温与短时的烧结方法可以避免处于晶界处的LSCO的CuO面被破坏,进而提高超导/铁磁复合材料中在晶界处的铁磁的共存含量.
参考文献
| [1] | Xu J T;Tan S;Pi L et al.Coexistence and Competition between Superconductivity and Magnetism in La2 x Srx Cu0 94 M0 06O4 (M ＝ Mn and Ru)[J].Journal of Applied Physics,2008,104(10):063914. |
| [2] | Wu H;Tan S;Wang WX;Zhang YH .Superconductivity in La1.85-4/3xSr0.15+4/3xCu1-xMnxO4 with x up to 0.2[J].Physical review, B. Condensed matter and materials physics,2005(14):4520-1-4520-6-0. |
| [3] | Cai, CB;Peng, L;Holzapfel, B;Xie, XM;Liu, ZY;Lu, YM;Chen, CZ .Proximity and reversal magnetoresistance behaviour in the oxide heterostructure of cuprate and manganite[J].Superconductor Science & Technology,2010(3):034010:1-034010:5. |
| [4] | Lin J G;Hsu Daniel;Song M Y et al.Thickness and Feld Dependent Superconductivity in YBa2Cu3O7/La0 7Sr0 3MnO3 Bilayers[J].Journal of Applied Physics,2010,107(03):09E130. |
| [5] | 龚红宇,全静,张玉军,毕见强,车松蔚.纳微米PZT/水泥基压电复合材料的研究[J].人工晶体学报,2010(03):687-690,695. |
| [6] | 邵磊,李爱菊,李腾,王鹏,贺信哲.环氧树脂/石墨双极板复合材料的性能分析[J].人工晶体学报,2009(02):305-308. |
| [7] | 次立杰,张绍岩,张玉军.BiVO4/SiO2复合材料的制备及光学性能[J].人工晶体学报,2010(03):797-801. |
| [8] | Hsu D;Kumary TG;Lin L;Lin JG .Coexistence of superconductivity and magnetism in the composite material (La1.85Sr0.15CuO4)(1-x)(La0.3Dy0.4Sr0.3MnO3)(x)[J].Physical review, B. Condensed matter and materials physics,2006(21):4504-1-4504-7-0. |
| [9] | Tkach A V;Ponomarev A I;Charikova TB et al.Electrical Resistance and Magnetic Properties of Double-Doped Ceramics La1 85-4/3xSr0 15+4/3x Cu1-xMnx O4[J].Low Temperature Physics,2007,33(07):257-263. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%