以KH550改性的纳米锑掺杂氧化锡粉体(ATO)与Bayhydrol XP 2593水性聚氨酯(WPU)分散体为原料,与成膜助剂、消泡剂、流平剂、附着力促进剂等复配,通过正交试验优化复合涂料的配方,制得了分散稳定的水性纳米ATO/聚氨酯复合涂料.助剂配方正交优化结果表明,以二乙二醇乙醚为成膜助剂、用量约3.0％,以Z-6040为附着力促进剂、用量约4.0％,以BYK094为消泡剂、用量约0.05％,以DuPont FSJ为流平剂、用量约0.1％,以WT-207为增稠剂、用量约0.06％,可以制得综合性能良好的ATO/WPU复合涂料,其涂膜铅笔硬度可达H、附着力1级,可见光透过率为83.6％,隔热效果良好,降温可达6.5℃.
参考文献
| [1] | 姚晨,赵石林,缪国元.纳米透明隔热涂料的特性与应用[J].涂料工业,2007(01):29-32. |
| [2] | 龚圣,李明子,皮丕辉,杨卓如.纳米锑掺杂氧化锡的研究进展[J].化工进展,2008(10):1516-1521. |
| [3] | Saadeddin I;Pecquenard B;Manaud JP;Decourt R;Labrugere C;Buffeteau T;Campet G .Synthesis and characterization of single- and co-doped SnO2 thin films for optoelectronic applications[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(12):5240-5249. |
| [4] | Aukkaravittayapun S;Wongtida N;Kasecwatin T;Charojrochkul S;Unnanon K;Chindaudom P .Large scale F-doped SnO2 coating on glass by spray pyrolysis[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(1):117-120. |
| [5] | 黄旭珊,潘亚美,吕维忠,罗仲宽.影响纳米ITO透明隔热涂料性能的因素[J].涂料工业,2010(08):33-35,42. |
| [6] | 聂鹏,赵学增,陈芳,王伟杰.基于欠膨胀射流的SiO2/环氧树脂纳米复合材料制备方法研究[J].高校化学工程学报,2005(06):834-838. |
| [7] | 龚圣,陈泽成,唐富龙,皮丕辉,文秀芳,郑大锋,程江,杨卓如.纳米锑掺杂氧化锡的制备及表征[J].硅酸盐学报,2009(04):648-652. |
| [8] | 何秋星,涂伟萍,胡剑青.透明隔热纳米涂料的研究进展[J].化工新型材料,2005(12):8-12. |
| [9] | 顾广新,章道彪,范军锋,魏勇,武新民.透明隔热涂料的制备及其在汽车上应用[J].涂料工业,2010(11):52-55,60. |
| [10] | 龚圣,廖列文,阎杰,杨卓如.透明隔热纳米复合涂料的制备及其性能研究[J].太阳能学报,2011(08):1195-1199. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%