采用热力学计算理论预测双相钢的临界退火温度,计算值与试验结果相符.根据铁素体和奥氏体体积分数比值为70∶30,计算得到退火温度为807℃.试验采用800℃的退火温度得到的最终组织马氏体体积分数为13 ％～18％,且其性能完全达到DP590双相钢级别要求.在临界退火和过时效段之间有至少10％～12％的奥氏体转变为新生铁素体和马氏体.
参考文献
| [1] | D. A. F. Bayton;G. Fourlaris .Dual phase versus CMn strip steels: comparison of quasi-static and dynamic connection properties for road safety barriers[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2011(1):85-90. |
| [2] | A. Kumar;S.B. Singh;K.K. Ray .Influence of bainite/martensite-content on the tensile properties of low carbon dual-phase steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):270-282. |
| [3] | Calixto Isaac GARCIA;Kengun CHO;Konstantin REDKIN .Influence of Critical Carbide Dissolution Temperature during Intercritical Annealing on Hardenability of Austenite and Mechanical Properties of DP-980 Steels[J].ISIJ International,2011(6):969-974. |
| [4] | Mohsen ASADI ASADABAD;Massoud GOODARZI;Shahram KHEIRANDISH .Kinetics of Austenite Formation in Dual Phase Steels[J].ISIJ International,2008(9):1251-1255. |
| [5] | Q L Yong.Secondary phases in steels[M].北京:冶金工业出版社,2006 |
| [6] | J. D. ROBSON;P. B. PRANGNELL .DISPERSOID PRECIPITATION AND PROCESS MODELLING IN ZIRCONIUM CONTAINING COMMERCIAL ALUMINIUM ALLOYS[J].Acta materialia,2001(4):599-613. |
| [7] | V Abouei,H Saghafian,Sh Kheirandish.Dry Sliding Oxidative Wear in Plain Carbon Dual Phase Steel[J].钢铁研究学报（英文版）,2007(04):43-48. |
| [8] | A Nouri,H Saghafian,Sh Kheirandish.Effects of Silicon Content and Intercritical Annealing on Manganese Partitioning in Dual Phase Steels[J].钢铁研究学报（英文版）,2010(05):44-50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%