以EDTA为螯合剂,采用络合共沉淀法合成了NaYF4:Er3+和NaYF4:Yb3+/Er3+纳米晶.分别采用XRD、SEM、荧光分光光度计对合成的样品进行了结构、形貌和上转换荧光分析.XRD结果表明,制备的NaYF4:Er3+和NaYF4:Yb3+/Er3+均为纯立方相;SEM结果显示,制备的NaYF4:Er3+和NaYF4: Yb3+/Er3+晶粒粒径都在100nm左右,与NaYF4:Er3+相比,NaYF4:Yb3+/Er3+晶粒尺寸分布更均匀,分散性更好,符合作为荧光标记材料的要求;上转换荧光分析表明,在980nm激光器激发下,NaYF4:Yb3+/Er3+的发光强度比NaYF4:Er3+提高了1个数量级.
参考文献
| [1] | 孙雅娟 .稀土上转换纳米材料的合成、表征、机理和表面动力学研究[D].长春:吉林大学,2007. |
| [2] | 杨奉真,衣光舜,陈德朴,程京.纳米NaYF4：Yb,Ho上转换荧光粉的合成及其性质研究[J].高等学校化学学报,2004(09):1589-1592. |
| [3] | Wang Guofeng;Qin Weiping;Zhang Jisen .Controlled synthesis and luminescence properties from cubic to hexagonal NaYF4:Ln3+ (Ln= Eu and Yb/Tm) microcrystals[J].Journal of Alloys and Compounds,2009,475(1-2):452. |
| [4] | 孙墨杰;贾若琨 .上转换材料NaYF4:Er3+,Yb3+纳米晶的制备[J].吉林大学自然科学学报,2006,44(05):803. |
| [5] | Suyver J F;Grimm J;Kramer K W et al.Highly efficient near-infrared to visible up-conversion process in NaYF4:Er3+ /Yb2+[J].Journal of Luminescence,2005,114(01):53. |
| [6] | Chatterjee DK;Rufaihah AJ;Zhang Y .Upconversion fluorescence imaging of cells and small animals using lanthanide doped nanocrystals.[J].Biomaterials,2008(7):937-943. |
| [7] | 黄敏文,孟繁谊,苑星海,李勇,刘茹.纳米NaY1-x-yF4：Yb3+y,Tm3+x材料的上转换光学特性[J].发光学报,2008(01):192-194. |
| [8] | 王猛,徐淑坤,杨冬芝.NaYF4：Yb,Er/Tm上转换荧光纳米材料的合成、修饰及应用[J].化学进展,2008(12):1880-1885. |
| [9] | 李岩 .稀土离子掺杂的NaYF<,4>上转换纳米晶的制备与表征[D].长春理工大学,2006. |
| [10] | 李珊珊 .上转换发光基质氟化钠纳米粒子的水相合成及形成机理[D].上海:东华大学,2007. |
| [11] | 窦京涛 .稀土上转换发光纳米材料的合成及其性质研究[D].北京交通大学,2008. |
| [12] | 王琼华,彭宝剑,李大海,辛燕霞,蒋泉.显示用上转换绿色发光材料NaYF4：Er,Yb及其特性[J].光子学报,2008(12):2508-2510. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%