采用Gleeble-3500热模拟试验机模拟了屈服强度500 MPa级高建钢热变形奥氏体的动态连续冷却转变过程,结合金相法绘制试验钢的CCT曲线,并对相变组织进行维氏硬度测试.试验结果表明,当冷速低于2.5℃/s时,形成多边形铁素体、针状铁素体和珠光体的混合组织;在5～30 ℃/s的冷速范围内,形成针状铁素体和粒状贝氏体的混合组织;在冷速50℃/s时,开始出现少量板条贝氏体组织.随着冷速的增大,组织细化,连续冷却转变组织硬度增加.试验钢两阶段变形后的控冷工艺窗口为5～25℃/s.
参考文献
| [1] | Xueming Wang;Hui Zhao;Chengjia Shang et al.The microstructure and properties of high performance steels with low yield-to-tensile ratio[J].Journal of Alloys and Compounds,2013,577(0 Supplement 1):678-683. |
| [2] | 白晓虹,陈焕德,岳重祥,刘东升.TMCP型F500船板钢显微组织及性能的研究[J].上海金属,2012(06):11-16. |
| [3] | 曹二转,孟献华,唐武峰.浅谈桥梁钢标准的发展[J].河南冶金,2008(01):26-29. |
| [4] | Lei Fan;Dehui Zhou;Tongliang Wang;Shurui Li;Qingfeng Wang.Tensile properties of an acicular ferrite and martensite/austenite constituent steel with varying cooling rates[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2014:224-231. |
| [5] | 泊勇;余伟;武会宾 等.优化控冷制度改善XI20管线钢的组织和性能[J].上海金属,2007,29(02):40-43. |
| [6] | 花桂泰;杨胜蓉.YB/T5127-93钢的临界点测定方法(膨胀法)[M].北京:中国标准出版社,1997 |
| [7] | 杨胜蓉.YB/T5129-93钢的连续冷却转变曲线图的测定方法(膨胀法)[M].北京:中国标准出版社,1997 |