研究了亚固相线温度扩散退火处理对FGH96粉末高温合金原始颗粒边界(PPB)的影响,结果表明,试验用热等静压(HIP)态FGH96试样中所存在的PPB主要由富Ti和Nb的MC型碳化物以及少量的氧化物组成.试样经1230℃×8h/AC扩散退火处理后并不能完全消除PPB,但部分碳化物溶解,PPB从连续网膜转变成离散的颗粒状,显微组织中PPB明显减轻.试样经HIP+1150℃×30min/WC处理后在PPB较严重的区域出现裂纹,主要沿PPB扩展;退火态试样经1230℃×30min/WC处理后裂纹相对较细,其主要沿晶界扩展.
参考文献
| [1] | 邹金文,汪武祥.粉末高温合金研究进展与应用[J].航空材料学报,2006(03):244-250. |
| [2] | Ingesten N G;Warren R;Winberg L.Nature and origin of previous particle boundary precipitates in P/M superalloys[A].Dordrecht:D Reidel Publishing Company,1982:1013. |
| [3] | 刘明东,张莹,刘培英,张义文.FGH95粉末高温合金原始颗粒边界及其对性能的影响[J].粉末冶金工业,2006(03):1-5. |
| [4] | 张义文,张凤戈,张莹,陶宇.一种消除粉末高温合金中PPB的方法[J].钢铁研究学报,2003(z1):513-518. |
| [5] | Warren R;Ingesten N G;Winberg L et al.Particle surfaces and prior particle boundaries in hafnium modified PM astroloy[J].Powder Metallurgy,1984,27(03):141. |
| [6] | Prakash T L;Tewari S N;Ramakrishnan P.Prior particle boundary(PPB) precipitates and the fractographic features of hot isostatically pressed(HIP) nimonic AP-1 P/M superalloy[A].Soitzerland:Trans Techn Publications,1985:402. |
| [7] | 毛健;俞克兰;周瑞发 .粉末预热处理对HIP René 95粉末高温合金组织的影响[J].粉末冶金技术,1989,7(04):213. |
| [8] | 牛连奎;张英才;李世魁 .粉末预热处理对FGH95合金组织和性能的影响[J].粉末冶金工业,1999,9(03):23. |
| [9] | 冯涤;李力 .IN 100高温合金粉末在加热过程中的相转变和原始颗粒边界问题[J].钢铁研究总院学报,1983,3(04):565. |
| [10] | Pierron X;Banik A;Maurer G E.Sub-solidus HIP process for P/M superalloy conventional billet conversion[A].US:The Minerals,Metals & Materials Society,2000:425. |
| [11] | 王淑云,李惠曲,谭勇,杨洪涛.热等静压FGH96合金热处理过程的组织[J].新技术新工艺,2008(11):103-105. |
| [12] | Rao G A;Srinivas M;Sarma D S .Effect of oxygen content of powder on microstructure and mechanical properties of hot isotatically pressed superalloy inconel 718[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2006,435-436:84. |
| [13] | Yang Wanhong;Mao Jian;Wang Wuxiang.Effects of heat treatment on prior particle boundary precipitation in a powder metallurgy nickel base superalloy[J].Adv Perfor Mater,1995(02):269. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%