By means of Gleeble-1500 dynamic thermomechanical simulator,the continuous casting process for HRB335C steel was simulated using solidifying method and hot ductility and strength of the steel were determined.The test results indicate that there are three temperature regions of brittleness for HRB335C billet in the temperature range from 700℃ to solidification point;the first temperature region of brittleness is 1 300℃ to solidification point of the billet,the second temperature region of brittleness is 1 200-1 000℃,and the third temperature region of brittleness is 700-850℃;the steel is plastic at 850-1 000℃.The cracking sensitivity was studied in the different temperature zones of the brittleness for steel HRB335C and the target surface temperature curve for the secondary cooling is determined.With optimized process,the mathematical model of the steady temperature field with two-dimensional heat transfer for 150 mm×150 mm HRB335C steel billet was established to optimize the secondary cooling process.The conic relation of water distribution between secondary cooling water flux and casting speed is regressed.Keeping the surface temperature of billet before the straightening point above 1 000℃,the results of billet test indicate that there is free central shrinkage cavity.The billet defect is decreased greatly,and the quality of billet is obviously improved.
参考文献
| [1] | WANG Xin-hua;WU Dong-mei .The Studying on the Brittle Character of Carbon Steel Slab[J].Iron and Steel,1997,32(zk):750. |
| [2] | Lankford W T Jr .Some Considerations of Strength and Ductility in the Continuous Casting Process[J].Metallurgical and Materials Transactions,1972,13(06):1331. |
| [3] | JB/T 7945-1999.JB/T 7945-1999.Methods for Testing the Mechanical Properties of Grey Cast Iron[S]. |
| [4] | Mintz B;Yue S;Jonas J .Hot Ductility of Steels and Its Relationship to the Problem of Transverse Cracking During Continuous Casting[J].International Materials Reviews,1991,36(05):187. |
| [5] | Tszeng T C;Kobayashi S .Stress Analysis in Solidification Processes:Application to Continuous Casting[J].International Journal of Machine Tools and Manufacture,1989,29(01):121. |
| [6] | Huespe A E .Visco-Plastic Constitutive Models of Steel at High Temperature[J].Journal of Materials Processing Technology,2000,102(I):143. |
| [7] | Kelly J E;Michalek K P .Initial Development of Thermal and Stress Fields in Continuously Cast Steel Billets[J].Metallurgical and Materials Transactions,1988,19A(10):2589. |
| [8] | R.Ghasemzadeh.A MATHEMATICAL HEAT TRANSFER MODEL IN STATIC AND CONTINUOUS CASTING[J].金属学报（英文版）,2004(06):776-784. |
| [9] | 王彪,谢植,汪灿荣,贾光霖,刘文红,马交成.基于射钉法的小方坯凝固过程数值模拟[J].铸造技术,2007(03):435-438. |
| [10] | M. El-Bealy;N. Leskinen;H. Fredriksson .Simulation of cooling conditions in secondary cooling zones in continuous casting process[J].Ironmaking & Steelmaking: Products and applications,1995(3):246-255. |
| [11] | Santos C A;Spire J A;Garcia A .Mathematical Modeling and Optimization Strategies Applied to the Continuous Casting of Steel[J].Engineering applications of artificial intelligence,2003,16(05):511. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%