研究了用K_2ZrF_6助浸法制造C/Al复合材料的工艺和K_2ZrF_6的助浸机理结果表明:K_2ZrF_6处理后,C,Al间的润湿性仍比SiC,Al间的差C,Al间的润湿主要靠大量的界面化学反应、这使得复合材料的制造十分困难;而SiC、Al间的润湿靠微量的SiC在Al中的溶解K在纤维或涂层中的扩散也可能起助浸作用Al液在极短时间内对SiC涂层后的纤维束或纤维预制件浸渍良好同时,将基体Si合金化后,获得了完整的CF/SiC/Al界面,圆满解决了C/Al复合材料的界面相容性和制造中的问题
The CF/Al composite seems hard to be forming, the wettability between car-bon fibres and Al, which is mainly because of their interfacial chemical reaction, is still poorthough it was treated by K_2ZrF_6 wetting promotion. While, the wettability between SiC andAl is dependent on dissolving a small amount of SiC, coating on carbon fibre, in Al melt. Thediffusion of K, in K_2ZrF_6, through the carbon fibre surface or SiC coating may perhaps bepromoted. Molten Al may fully infiltrate the SiC coated fibre tows or fibre preforms in a veryshortterm. Thus, the fair CF/SiC/Al interfaces may be obtained by alloying the matrixwith Si, and the compattibility between C/Al interfaces and other forming problem may be
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%