为制备贮存稳定性优良的紫外光(UV)固化涂料,采用自制改性环氧丙烯酸酯树脂、活性稀释剂、光引发剂和阻聚剂制备了UV固化涂料体系并通过考察50℃下贮存7d前后黏度的变化,研究了活性稀释剂、光引发剂和阻聚剂种类及用量对贮存稳定性的影响,并确定了最优体系:活性稀释剂w(己二醇二丙烯酸酯)=20％ ～ 30％,光引发剂w(Darocur 11733)=3.0％,阻聚剂w(对羟基苯甲醚)=0.04％.用红外光谱、凝胶渗透色谱等对贮存前后的体系进行了表征.测试了以最优体系为基础配制的UV涂料的涂膜性能.结果表明,加速贮存7d后,涂料体系的重均分子量和数均分子量分别增加393 g/mol和403 g/mol,C=C双键含量仅损失4.9％,可见涂料具有较好的贮存稳定性,其漆膜性能与贮存前相比并无差异.
参考文献
| [1] | Mishra, RS;Mishra, AK;Raju, KVSN .Synthesis and property study of UV-curable hyperbranched polyurethane acrylate/ZnO hybrid coatings[J].European Polymer Journal,2009(3):960-966. |
| [2] | Xiao, XY;Hao, CC .Preparation of waterborne epoxy acrylate/silica sol hybrid materials and study of their UV curing behavior[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2010(1/3):82-87. |
| [3] | 余宗萍,成伟,杨鹏飞.热塑性丙烯酸酯树脂在紫外光固化涂料中的应用[J].上海涂料,2013(12):1-4. |
| [4] | Bajpai M;Shukla V;Habib F .Development of a heat resistant UV-curable epoxy coating[J].Progress in Organic Coatings: An International Review Journal,2005(4):239-245. |
| [5] | 张银钟 .UV固化三官能度聚氨酯丙烯酸酯胶粘剂的制备与性能研究[D].柳州:广西工学院,2012. |
| [6] | 李飞,段华军,王钧,李孝兰.复配阻聚剂对改性UPR贮存稳定性的影响研究[J].塑料工业,2012(08):93-95,106. |
| [7] | 肖俊芳 .低温光-热双重固化的紫外光固化涂料[D].广州:华南理工大学,2012. |
| [8] | 刘登良.涂料工艺(上册)[M].北京:化学工业出版社,2010 |
| [9] | 余宗萍,廖申伟,罗荣荣.常用光引发剂在紫外光固化涂料中的应用研究[J].上海涂料,2010(08):13-16. |
| [10] | 杨文玮,刘华,钱建华,刘坐镇.阻聚剂对酚醛环氧乙烯基酯的贮存及固化影响[J].热固性树脂,2012(02):20-24. |
| [11] | 潘祖仁.高分子化学[M].北京:化学工业出版社,2011 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%