研究了不同时效温度下的沉淀硬化不锈钢0Cr14Ni5Mo2Cu2Nb的TEM组织、硬度和冲击韧性.结果表明:时效过程中,0Cr14Ni5Mo2Cu2N钢主要以ε-Cu相析出为主.时效温度为420℃时,Cu以细小共格ε-Cu相析出,导致0Cr14Ni5Mo2Cu2N钢的硬度达到峰值,而韧性最差,冲击断口以解理为主.随着时效温度增加,ε-Cu相逐步脱溶长大,基体再结晶,硬化程度逐步降低,韧性升高,冲击断口逐步过渡为全韧窝形貌.0Cr14Ni5Mo2Cu2Nb钢的韧性主要决定于冲击裂纹扩展功.时效组织对0Cr14Ni5Mo2Cu2Nb钢冲击裂纹形成功影响较小,对裂纹扩展功有着较大影响.
参考文献
| [1] | Nakagawa H .[J].Journal of Materials Science,2000,35:2245. |
| [2] | Habibi Bajguirani H R .[J].Materials Science and Engineering,2002,A338:142. |
| [3] | Mats Hattestrand;Jan-Olof Nilsson;Krystyna Stiller;Ping Liu;Marcus Andersson .Precipitation hardening in a 12%Cr–9%Ni–4%Mo–2%Cu stainless steel[J].Acta materialia,2004(4):1023-1037. |
| [4] | Llewellyn D T .[J].Ironmaking and Steelmaking,1996,22(01):25. |
| [5] | Tomposon S W .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1996,27A:1573. |
| [6] | Bhagat A N .[J].ISIJ International,2004,44(01):198. |
| [7] | Deschamps A .[J].ISIJ International,2003,43(11):1826. |
| [8] | 肖福仁 .[J].金属热处理,1999,20(04):35. |
| [9] | Chen Qing .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1995,26(02):417. |
| [10] | Chuang Y .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1984,15A:1921. |
| [11] | Krishnadev M R .[J].Metallurgical and Materials Transactions,1975,6:222. |
| [12] | Habibi H R .[J].ACTA METALLURGICA ET MATERIALIA,1993,41(05):1613. |
| [13] | Kimura Y .[J].ISIJ International,1997,37(03):290. |
| [14] | Wriedt H A .[J].Transactions of the Metallurgical Society of AIME,1960,218(02):30. |
| [15] | Viswanathan U K.[J].Materials Science and Technology,1989(05):346. |
| [16] | Goodman S R.[J].Tr Met Trans,1973(02):2363. |
| [17] | Nakagawa H .[J].Journal of Materials Science,1999,34:3901. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%