研究Zn对Mg-Mn合金微观组织、力学性能和在Hank's溶液中腐蚀性能的影响.结果表明:Zn可以明显细化Mg-Mn合金的铸态组织,当合金中Zn含量(质量分数)为3%时,合金的晶粒尺寸由700~900 μm减小到50~80 μm.合金的力学性能也随Zn含量的增加而显著提高;Zn含量为3%时,拉伸强度提高128.8 MPa,屈服强度提高42.6 MPa,伸长率提高1倍多.在Mg-Mn合金中加入 1%~2%的Zn,能够增强Mg-Mn合金钝化膜的稳定性,使Mg-Mn合金腐蚀速度显著降低.但是,当Zn含量增至3%时,钝化膜变得不稳定,腐蚀速度增加,耐蚀性能降低.
参考文献
| [1] | CAHN R W;HAASEN P;KRAMER E J.Materials science and technology[M].New York:VCH Publishers Inc,1996:18-20. |
| [2] | Witte F;Fischer J;Nellesen J;Crostack HA;Kaese V;Pisch A;Beckmann F;Windhagen H .In vitro and in vivo corrosion measurements of magnesium alloys[J].Biomaterials,2006(7):1013-1018. |
| [3] | Witte F;Kaese V;Haferkamp H;Switzer E;Meyer Lindenberg A;Wirth CJ;Windhagen H .In vivo corrosion of four magnesium alloys and the associated bone response.[J].Biomaterials,2005(17):3557-3563. |
| [4] | Staiger MP;Pietak AM;Huadmai J;Dias G .Magnesium and its alloys as orthopedic biomaterials: A review[J].Biomaterials,2006(9):1728-1734. |
| [5] | ZHANG Er-lin;XU Li-ping;YANG Ke .Formation by ion plating of Ti-coating on pure Mg for biomedical applications[J].Scripta Materialia,2005,53(05):523-527. |
| [6] | 王登峰,张金山,杜宏伟,许春香,王红霞,韩富银,赵兴国,梁伟.镁锰合金的晶粒细化及其耐蚀性的研究[J].铸造设备研究,2005(01):12-14. |
| [7] | 关学丰.改善变形Mg-Mn系合金性能的研究[J].湖南冶金,1993(01):7-9. |
| [8] | 范靖亚;康广范 .Mg-Y-Mn合金高性能板材研究[J].轻合金加工技术,1994,22(08):45-47. |
| [9] | 翁康荣,赵红岩,周占霞,赵红亮.Si、Ca对Mg-2Mn变形镁合金组织和性能的影响[J].热加工工艺,2006(01):1-3. |
| [10] | BALLERINI G;BARDI U;BIGNUCOLO R;CERAOLO G .About some corrosion mechanisms of AZ91D magnesium alloy[J].Corrosion Science,2005,47(09):2173-2184. |
| [11] | 张忠林,刘兆晶,李凤珍.镁合金燃点和耐蚀性及力学性能的研究[J].轻合金加工技术,2003(07):31-34. |
| [12] | 李冠群,吴国华,樊昱,丁文江.主要合金元素对镁合金组织及耐蚀性能的影响[J].铸造技术,2006(01):79-83. |
| [13] | 谢苗,王斌,邓海燕,甘纯玑.海带膳食纤维的制备条件与营养评价[J].河南科技大学学报（农学版）,2004(04):56-59. |
| [14] | 胡汉起.金属凝固原理[M].北京:机械工业出版社,2000:126-130. |
| [15] | D. Qiu;M.-X. Zhang;J.A. Taylor .A novel approach to the mechanism for the grain refining effect of melt superheating of Mg-Al alloys[J].Acta materialia,2007(6):1863-1871. |
| [16] | MA Yan-long,PAN Fu-sheng,ZUO Ru-lin,ZHANG Jin,YANG Ming-bo.Effects of heat-treatment on microstructure of wrought magnesium alloy ZK60[J].中国有色金属学会会刊（英文版）,2006(z3):1888-1891. |
| [17] | BARIL G;PEBERE N .The corrosion of pure magnesium in aerated and deaerated sodium sulphate solutions[J].Corrosion Science,2001,43(03):471-484. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%