碳纤维/环氧树脂(C/EP)复合材料制孔毛刺和撕裂缺陷,对构件的装配精度影响较大.为了揭示C/EP复合材料制孔毛刺和撕裂缺陷的形成机制,采用微米划痕试验研究沿不同纤维方向切削加工时材料的破坏去除过程,并用FEI公司Quanta 200环境扫描电镜对划切后的沟槽及切屑的形貌进行观察分析.结果表明:当划切方向与纤维方向垂直时,划切力最大,较易产生撕裂缺陷;当划切方向与纤维方向呈30°、45°和60°时,划痕左侧纤维受到压头挤压向左退让并弯曲,产生锯齿形断裂,否则形成毛刺;划痕右侧纤维为避让压头发生较大的弯曲变形,纤维断裂均匀,不容易形成毛刺.理论分析和划痕试验结果表明:制孔加工时,纤维方向与刀具旋转方向成钝角的区域容易产生毛刺缺陷,与刀具旋转方向成锐角的区域边缘光滑,与刀具旋转方向垂直的区域容易形成撕裂缺陷;出口缺陷与试验结果一致.
参考文献
| [1] | 韦红余,陈文亮,蒋红宇,等.面向现代飞机装配的长寿命机械连接技术[J].航空制造技术,2009(17):34-37.Wei Hongyu,Chen Wenliang,Jiang Hongyu,et al.Longlife mechanical connecting technology for modern aircaft assembly[J].Aeronautical Manufacturing Technology,2009(17):34-37. |
| [2] | Abrao A M,Faria P E,Campos Rubio J C,et al.Drilling of fiber reinforced plastics:a review[J].Journal of Materials Processing Technology,2007,186:17. |
| [3] | Zhang H J,Chen W Y,Chen D C,et al.Assessment of the exit defects in carbon fibre-reinforced plastic plates caused by drilling[J].Key Engineering Materials,2001,196:43-52. |
| [4] | Hocheng H,Tsao C C.The path towards delamination-free drilling of composite materials[J].Journal of Materials Processing Technology,2005,167:251-264. |
| [5] | Upadhyay P C,Lyons J S.On the evaluation of critical thrust for delamination-free drilling of composite laminates[J].Journal of Reinforced Plastics and Composites,1999,18:1287-1303. |
| [6] | Davim J P,Pedro R.Drilling carbon fiber reinforced plastics manufactured by autoclave-experimental and statistical study[J].Materials and Design,2003,24:315-324. |
| [7] | Durāo L M P,Goncalves DJ S,Tavares J M R S,et al.Drilling tool geometry evaluation for reinforced composite laminates[J].Composite Structures,2010,92:1545-1550. |
| [8] | Pwu H Y,Hocheng H.Chip formation model of cutting fiber-reinforced plastics perpendicular to fiber axis[J].Transactions of the ASME,1998,120:192-196. |
| [9] | Wang X M,Zhang L C.An experimental investigation into the orthogonal cutting of unidirectional fiber reinforced plastics[J].International Journal of Machine Tools & Manufacture,2003,43:1015-1022. |
| [10] | 张伟,艾启兰,刁锐,等.碳纤维复合材料切削后表面微观分析[J].大连轻工业学院学报,1999,18(3):242-246.Zhang Wei,Ai Qilan,Diao Rui,et al.Microanalysis for the drilling cutting surface of the carbon fibre reinforced composite material[J].Journal of Dalian Institute of Light Industry,1999,18(3):242-246. |
| [11] | 张厚江,陈五一,陈鼎昌.碳纤维复合材料(CFRP)孔壁的微观形态[J].复合材料学报,2000,17(2):98-101.Zhang Houjiang,Chen Wuyi,Chen Dingchang.Microstructure of the hole surface of CFRP[J].Acta Materiae Compositae Sinica,2000,17(2):98-101. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%