研究了高压下凝固Ti-48Al合金片层间距及其力学性能的变化.结果表明,压力下凝固时,随着凝固压力的增加扩散系数降低,从而引起片层增厚速度的降低,即片层间距的减小.在常压、2 GPa、4 GPa下凝固时,片层间距的平均值分别为495,345,227 nm.片层组织的显微硬度随着凝固压力的增加而增加.该实验为细化片层间距提供了一种新的方法.
参考文献
| [1] | Wang WH;Dong C;Shek CH .Bulk metallic glasses[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(2/3):45-89. |
| [2] | Merkel S et al.[J].Physics of the Earth and Planetary Interiors,2004,145:239. |
| [3] | Paszkowicz W .[J].Nucleat Instrument and Methods in Physics Research B,2002,198:142. |
| [4] | Emmunauel S et al.[J].Journal of Sold State Chemistry,2004,177:299. |
| [5] | Batashef A E ed.金属和合金在压力下的结晶[M].Harbin:Harbin Institute of Technology Publisher,1987:11. |
| [6] | 胡汉起.金属凝固原理[M].北京:机械工业出版社,2000:46. |
| [7] | 秦高梧.Ti-Al系金属间化合物[J].稀有金属材料与工程,1995(02):1-7. |
| [8] | Mccullough C et al.[J].Acta Metallurgica,1989,37:1321. |
| [9] | Ramanujan R V.[J].International Materials Reviews,2000(45):217. |
| [10] | A Denquin;S Naka .[J].Acta Metallurgica,1995,43:343349. |
| [11] | 曹国鑫,林建国,孙志鹏,张永刚,陈昌麒.晶粒尺度和片层厚度对全片层γ-TiAl合金性能的影响[J].稀有金属材料与工程,2000(03):172-176. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%