The cracking behaviour of X-70 pipeline steel in near-neutral pH solutions was studied under different modes of cyclic loading. The crack propagation process of X-70 pipeline steel under low frequency cyclic loading condition was controlled mainly by stress corrosion cracking (SCC) mechanism. Under mixed-mode cyclic loading, both higher tensile stress and shear stress made cracks easier to propagate. Applied cathodic potentials and high content of carbon dioxide in solutions also promoted the propagation of cracks. The propagation directions of cracks were different under different cyclic loading conditions. Under mode I (pure tensile stress) cyclic loading condition, cracks were straight and perpendicular to the tensile stress axis, while under mixed-mode Ⅰ/Ⅲ (tensile/shear stress) cyclic loading,cracks were sinuous and did not propagate in the direction perpendicular to the main tensile stress axis. Under the mixed-mode cyclic loading, cracks were much easier to propagate, suggesting that shear stress intensified the role of tensile stress. In addition, shear stress promoted the interaction between cracks, resulting in easier coalescence of cracks.
参考文献
| [1] | National Energy Board.Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil[M].Gas Pipelines MH-2-95 Canada,1996:36. |
| [2] | M. Yunovich;Z. Xia;Z. Szklarska-Smialowska .Factors influencing stress corrosion cracking of carbon steel in diluted bicarbonate environments[J].Corrosion: The Journal of Science and Engineering,1998(2):155-161. |
| [3] | J.G. Gonzalez-Rodriguez;M. Casales;V.M. Salinas-Bravo .Effect of Microstructure on the Stress Corrosion Cracking of X-80 Pipeline Steel in Diluted Sodium Bicarbonate Solutions[J].Corrosion: The Journal of Science and Engineering,2002(7):584-590. |
| [4] | W. Chen;F. King;E. Vokes .Characteristics of Near-Neutral-pH Stress Corrosion Cracks in an X-65 Pipeline[J].Corrosion: The Journal of Science and Engineering,2002(3):267-275. |
| [5] | B. Gu;W. Z. Yu;J. L. Luo;X. Mao .Transgranular stress corrosion cracking of X-80 and X-52 pipeline steels in dilute aqueous solution with near-neutral pH[J].Corrosion: The Journal of Science and Engineering,1999(3):312-318. |
| [6] | B Delanty;J O'Beirne .[J].Oil & Gas Journal,1992,P15:39. |
| [7] | R N Parkins;W K Blanchard;B S Delanty .[J].Corrosion,1994,50(05):394. |
| [8] | M J Wilmott;R L Sutherby.1998 International Pipeline Conference[C].ASME,1998:409. |
| [9] | R.B. Rebak;Z. Xia;R. Safruddin .Effect of Solution Composition and Electrochemical Potential in Stress Corrosion Cracking of X-52 Pipeline Steel[J].Corrosion: The Journal of Science and Engineering,1996(5):396-405. |
| [10] | T Kushida;K Nose;H Asahi;M Kimura,Y Yamane,S Endo,H Kawano.Corrosion/2001, NACE International[M].Houston TX,2001 |
| [11] | B. Gu;J. Luo;X. Mao .Hydrogen-facilitated anodic dissolution-type stress corrosion cracking of pipeline steels in near-neutral pH solution[J].Corrosion: The Journal of Science and Engineering,1999(1):96-106. |
| [12] | M. Puiggali;S. Rousserie;M. Touzet .Fatigue Crack Initiation on Low-Carbon Steel Pipes in a Near-Neutral-pH Environment Under Potential Control Conditions[J].Corrosion: The Journal of Science and Engineering,2002(11):961-970. |
| [13] | G Gabetta;S D Liberto;A Bennardo.Corrosion/2000, NACE International[M].Houston TX,2000 |
| [14] | R.N. Parkins;J.A. Beavers .Some Effects of Strain Rate on the Transgranular Stress Corrosion Cracking of Ferritic Steels in Dilute Near-Neutral-pH Solutions[J].Corrosion: The Journal of Science and Engineering,2003(3):258-273. |
| [15] | S B Lambert;J A Beavers;B Delanty.2000 International Pipeline Conference[C].ASME,2000:961. |
| [16] | J A Beavers;C L Durr;B S Delanty;D M Owen,R L Sutherby.Corrosion/2001, NACE International[M].Houston TX,2001 |
| [17] | X. -Y. Zhang;S. B. Lambert;R. Sutherby;A. Plumtree .Transgranular stress corrosion cracking of X-60 pipeline steel in simulated ground water[J].Corrosion: The Journal of Science and Engineering,1999(3):297-305. |
| [18] | B A Harle;J A Beavers .[J].Corrosion,1993,49(10):861. |
| [19] | J T Johnson;C L Durr;J A Beavers;B S Delanty.Corrosion/2000, NACE International[M].Houston TX,2000 |
| [20] | S B Lanbert;A Plumtree;R L Sutherby.Corrosion/2000, NACE International[M].Houston TX,2000 |
| [21] | S.-H. Wang;W. Chen;F. King .Precyclic-Loading-Induced Stress Corrosion Cracking of Pipeline Steels in a Near-Neutral-pH Soil Environment[J].Corrosion: The Journal of Science and Engineering,2002(6):526-534. |
| [22] | S H Wang;W X Chen;T Jack.2000 International Pipeline Conference[C].ASME,2000:1005. |
| [23] | J A Beavers;J T Johnson;R L Sutherby.2000 International Pipeline Conference[C].ASME,2000:979. |
| [24] | Y Z Wang;R W Revie;M T Shehata.International Pipeline Conference[C].ASME,1998:529. |
| [25] | F King;T Jack;W X Chen;S H Wang,E Mimoun,R W Revie,W Robert,D Phil.Corrosion/2001,NACE International[M].Houston TX,2001 |
| [26] | R N Parkins.Corrosion/2000, NACE International[M].Houston TX,2000 |
| [27] | J Q Wang;A Atrens;D R Cousens;N Kinaev .[J].Journal of Materials Science,1999,34:1721. |
| [28] | U Sharma;D G Ivey.2000 International Pipeline Conference[C].ASME,2000:193. |
| [29] | W X Chen;S H Wang;F King.2000 International Pipeline Conference[C].ASME,2000:953. |
| [30] | J Bulger;J L Luo.2000 International Pipeline Conference[C].ASME,2000:947. |
| [31] | W X Chen;F King;T R Jack;M J Wilmott .[J].Metallurgical and Materials Transactions,2002,33A:1429. |
| [32] | B T Lu;J L Luo;B McCrady.Proc of IPC'02 4th International Pipeline Conference[C].Calgary Alberta Canada IPC2002-27234 |
| [33] | H Guo;G F Li;X Cai;J S Bai,W Yang.Asian Pacific Conference on Fracture and Strength[C].Korea,2004 |
| [34] | Y.-Z. WANG;K. EBTEHAJ;D. HARDIE;R. N. PARKINS .THE BEHAVIOUR OF MULTIPLE STRESS CORROSION CRACKS IN A Mn-Cr AND A Ni-Cr-Mo-V STEEL: I-METALLOGRAPHY[J].Corrosion Science,1995(11):1651-1675. |
| [35] | Qinghua DU.Materials Mechanics[M].北京:人民教育出版社,1963:79. |
| [36] | R.H. Jones;H. Li;J.P. Hirth .Effects on Mixed-Mode I/III Loading on Environment-Induced Cracking[J].Corrosion: The Journal of Science and Engineering,2001(1):52-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%