利用SEM和TEM,对固溶强化合金Hastelloy C-276的初始组织和在650℃、不同拉应力下持久断裂试样进行显微组织分析.结果表明:试样的断口以典型的韧窝形貌为主,局部有少许晶间断裂现象,显示出C-276合金具有良好的高温韧性.在C-276合金的初始组织中,有退火孪晶和大量位错存在;在经受高应力拉伸过程中,晶体内产生大量形变孪晶;同时,发现在晶界和晶内有细小弥散的析出物.因此,C-276合金在650℃下优越的高温持久抗力是固溶强化、沉淀强化以及可能的孪晶强化综合作用的结果.
参考文献
| [1] | Cieslak M J et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1986,17A:2035. |
| [2] | Lioyd A C et al.[J].Electrochimica Acta,2004,49:3015. |
| [3] | Ahmad M et al.[J].Journal of Alloys and Compounds,2005,390:88. |
| [4] | Kim WG;Yin SN;Ryu WS;Chang JH;Kim SJ .Tension and creep design stresses of the "Hastelloy-X" alloy for high-temperature gas cooled reactors[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(0):495-497. |
| [5] | Turchi PEA;Kaufman L;Liu ZK .Modeling of Ni-Cr-Mo based alloys: Part I - phase stability[J].Calphad: Computer Coupling of Phase Diagrams and Thermochemistry,2006(1):70-87. |
| [6] | 蒋有荣.[A].Beijing:China's Nuclear Society,2007 |
| [7] | Leonard R B .[J].Corrosion,1969,25(05):222. |
| [8] | Akhter J I et al.[J].Journal of Materials Science Letters,2001,20:333. |
| [9] | Zhao J C et al.[J].Materials Science and Engineering A,2000,A293:112. |
| [10] | Nedjad S H et al.[J].Materials Science and Engineering A,2008,490:105. |
| [11] | Qin X Z et al.[J].Materials Letters,2008,62:58. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%