采用荧光紫外辐照UVB+冷凝的人工加速试验对丙烯酸聚氨酯清漆进行老化试验,用电化学阻抗谱(EIS)评价不同暴露时间涂层的屏障性.结果表明:随着暴露时间增加,一定频率下的低频阻抗模值|Z|下降,表现为时间的变化函数;傅立叶变换红外光谱(FTIR)分析表明,紫外暴露下发生高分子断链涂层降解,而在老化12天后|Z|值的升高可能与分子的重构变化有关;因而,EIS谱的|Z|值可作为一种较为有效的表征参数来反映UV老化后有机涂层的防护性能.
参考文献
| [1] | L.F.E.Jacques .Accelerated and outdoor/natural exposure testing of coatings[J].Progress in Polymer Science,2000(9):1337-1362. |
| [2] | Bauer DR. .Global exposure models for automotive coating photo-oxidation[J].Polymer Degradation and Stability,2000(3):297-306. |
| [3] | L. Fedrizzi;A. Bergo;M. Fanicchia .Evaluation of accelerated aging procedures of painted galvanised steels by EIS[J].Electrochimica Acta,2006(8/9):1864-1872. |
| [4] | 徐永祥,严川伟,丁杰,高延敏,曹楚南.紫外光对涂层的老化作用[J].中国腐蚀与防护学报,2004(03):168-173. |
| [5] | 杨丽霞,张三平,林安,潘莹,程学群.有机涂层渗水率及金属界面腐蚀的研究进展[J].材料保护,2001(10):28-30. |
| [6] | Bierwagen G.;Tallman D.;Li JP.;He LY.;Jeffcoate C. .EIS studies of coated metals in accelerated exposure[J].Progress in Organic Coatings: An International Review Journal,2003(2):148-157. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%