采用固.气反应球磨制备纳米晶MgH2粉末,测定纯镁粉在球磨过程中的吸氢动力学曲线.借助X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)等分析手段,研究Mg-H2反应球磨过程中的相结构与粉末形貌演变规律.结果表明,在机械球磨驱动作用下,Mg的吸氢过程可分为"缓慢-快速-饱和"3个阶段,其相组成分别对应"Mg(H)-Mg(H)+MgH2-MgH2".在0.5 MPa氢气压条件下,球磨21 h可使Mg完全氢化,获得粉末粒度1～3μm、晶粒尺寸10 nm左右的纳米晶MgH2粉末,其实际氢含量高达7.03%(质量分数,下同).
参考文献
| [1] | Bowman R C;Fultz B .[J].MRS Bulletin,2002,27(09):688. |
| [2] | HU Lian-xi,WANG Er-de.Hydrogen generation via hydrolysis of nanocrystalline MgH2 and MgH2-based composites[J].中国有色金属学会会刊（英文版）,2005(05):965-970. |
| [3] | Oelerich W;Klassen T;Bormann R .[J].Journal of Alloys and Compounds,2001,315(1-2):237. |
| [4] | Revesz A;Fatay D;Zander D et al.[J].JMetast Nanocr Mater,2005,24-25:447. |
| [5] | Chou K C;Li Q;lin Q et al.[J].International Journal of Hydrogen Energy,2005,30(03):301. |
| [6] | Zaluska A;Zaluski L;Strom-Olsen J O .[J].Journal of Alloys and Compounds,1999,288:217. |
| [7] | Liang Guoxian;Wang Erde;Fang Shoushi .[J].Journal of Alloys and Compounds,1995,223:111. |
| [8] | Hout J;Liang G;Boily S et al.[J].Journal of Alloys and Compounds,1999,293-295:495. |
| [9] | Zaluska A;Zaluski L;Strom-Oisen J O .[J].Journal of Alloys and Compounds,1999,289:197. |
| [10] | Fan Y H;Zhang S Q;Liao S J et al.[J].Chinese Journal of Catalysis,1999,20(05):490. |
| [11] | 王正品;张路;要玉宏.金属功能材料[M].北京:化学工业出版社,2004:9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%