The mierostrueture development of oxide scale on pure iron under the mutual action of compressive stress and cooling conditions was investigated. Oxide scale structure was examined by optical microscopy (OM) and scan-ning electron microscopy (SEM). It was found that oxide scale formed under normal cooling conditions had a struc-ture mainly consisting of an outer magnetite and an inner wustite layer. When a compressive stress was applied, nu-merous magnetite precipitates formed within wustite layer homogeneously at starting cooling temperature of 900℃, and the wustite layer in the scale was transformed into a mixture of mostly magnetite/iron eutectoid and magnetite layer at starting cooling temperature of 700 ℃. The wustite decomposition and precipitation of magnetite in wustite under compressive stress were discussed.
参考文献
| [1] | Roberts W L.Hot Rolling of Steel[M].New York,USA:Marcel Dekker,Inc,1983 |
| [2] | Guo R M;Too J J M.Recent Advances in Heat Transfer and Micro-Structure Modelling for Metal Processing[M].OH:ASME,Metals Park,1995 |
| [3] | Gao W;Li Z W.Developments in High-Temperature Corrosion and Protection of Materials[M].Cambridge:Woodhead Publishing Ltd,2008 |
| [4] | Massalski T B;Okamoto H;Subramanian P R.Binary Alloy Phase Diagrams[M].OH:ASME,Metals Park,1990 |
| [5] | R. V. Chen;W. V. D. Vuen .A Study of the Scale Structure of Hot-Rolled Steel Strip by Simulated Coiling and Cooling[J].Oxidation of Metals,2000(5/6):539-560. |
| [6] | Chen R Y;Yuen W Y D .Review of the High-Temperature Oxidation of Iron and Carbon Steels in Air or Oxygen[J].Oxidation of Metals,2003,59(5/6):433. |
| [7] | Cben R Y;Yuen W Y D .Oxidation of Low-Carbon,Low-Silicon Mild Steel at 450-900℃ Under Conditions Relevant to Hot-Strip Processing[J].Oxidation of Metals,2002,57(1/ 2):53. |
| [8] | Baud J;Ferrier A;Manenc J .Study of Magnetite Film Formation at Metal-Scale Interface During Cooling of Steel Products[J].Oxidation of Metals,1978,12(04):331. |
| [9] | Rolls R;Shahhosseini M H .Effect of Creep on the Oxidation Characteristics of Fe-Si Alloys at 973--1073 K[J].Oxidation of Metals,1982,18(3/4):115. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%