以Lutensol TO(异构十三醇聚氧乙烯醚)系列非离子表面活性剂为辅助剂,采用溶胶-凝胶法制备了比表面积高、孔径分布窄的锐钛矿型 TiO2 多孔微球,并用透射电镜、扫描电镜、热重-差热分析、X射线衍射和氮吸附进行了表征.以亚甲基蓝降解为模型反应评价了其光催化性能,并与商品化TiO2 Degussa P25进行了比较.实验结果表明,样品在425 ℃焙烧后,形成具有孔状结构的锐钛矿型TiO2微球,粒径为0.7～1.0 μm,比表面积为70.5 m2/g,总孔容为0.12 cm3/g,平均孔径为4.26 nm,晶粒尺寸为12 nm.这种多孔TiO2微球具有较高的催化活性,与Degussa P25纳米TiO2的催化活性相当.
参考文献
| [1] | Hoffmann M R;Martin S T;Choi W Y;Bahnemann D W .[J].Chemical Reviews,1995,95(01):69. |
| [2] | Rajeshwar K .[J].Journal of Applied Electrochemistry,1995,25(12):1067. |
| [3] | Dillert R;Cassano A E;Goslich R;Bahnemann D .[J].Catalysis Today,1999,54(2-3):267. |
| [4] | Noorjahan M.;Kumari VD.;Subrahmanyam M.;Boule P. .A novel and efficient photocatalyst: TiO2-HZSM-5 combinate thin film[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2004(3):209-213. |
| [5] | Sabate J;Anderson M A;Aguado M A;Gimenez J Cervera-March S Hill C G .[J].Journal of Molecular Catalysis,1992,71(01):57. |
| [6] | Byrne J A;Eggins B R;Brown N M D;McKinney B Rouse M .[J].Applied Catalysis B:Environmental,1998,17(1-2):25. |
| [7] | 徐志兵,郭畅,隆兴兴,唐业仓,魏先文.三维大孔TiO2光催化剂的制备及其催化性能[J].催化学报,2006(08):732-736. |
| [8] | 向礼琴,尹剑波,高文帅,赵晓鹏.准单分散球形二氧化钛颗粒的可控制备研究[J].无机材料学报,2007(02):253-258. |
| [9] | Widoniak J;Eiden-Assmann S;Maret G .Synthesis and characterisation of porous and non-porous monodisperse TiO2 and ZrO2 particles[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2005(0):329-334. |
| [10] | Eiden-Assmann S.;Widoniak J.;Maret G. .Synthesis and characterization of porous and nonporous monodisperse colloidal TiO2 particles[J].Chemistry of Materials,2004(1):6-11. |
| [11] | Zhang B L;Chen B S;Shi K Y;He S J Liu X L Du Z J Yang K L .[J].Applied Catalysis B:Environmental,2003,40(04):253. |
| [12] | 范晓星,于涛,邹志刚.介孔TiO2的材料合成及其在光催化领域的应用[J].功能材料,2006(01):6-9. |
| [13] | 李玲.表面活性剂与纳米技术[M].北京:化学工业出版社,2004:134. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%