在活性激发剂的作用下,利用矿渣、磷石膏(PG)和水泥混合制备磷石膏基胶凝材料(PGS),然后研究砂率和粉煤灰掺量对PGS砂浆性能的影响.结果表明:当激发剂掺量为3％时,20℃(湿度大于70％)养护28d的PGS固化体的抗压强度和抗折强度(41.9MPa和7.1MPa)分别较未掺激发剂时提高了89.6％和73.2％,28d软化系数为0.94;PGS固化体28d的总孔隙率(12.21％)较7d的总孔隙率降低了46.8％；当砂率为1∶1时,磷石膏砖的性能最佳,28d的抗压强度和抗折强度分别为56.9MPa和4.8MPa;当粉煤灰掺量为20％时,磷石膏砖的28d抗压强度和抗折强度分别为35.8MPa和3.3MPa,28d吸水率和软化系数分别为2.3％和0.90,质量损失率、抗压强度损失率和抗折强度损失率分别为1.9％、5.5％和4.3％.
参考文献
| [1] | John S. McCartney;Russell E. Berends .Measurement of filtration effects on the transmissivity of geocomposite drains for phosphogypsum[J].Geotextiles and geomembranes,2010(2):p.226. |
| [2] | Liping Ma;Ping Ning;Shaocong Zheng .Reaction Mechanism and Kinetic Analysis of the Decomposition of Phosphogypsum via a Solid-State Reaction[J].Industrial & Engineering Chemistry Research,2010(8):3597-3602. |
| [3] | Othman I;Al-Masri MS .Impact of phosphate industry on the environment: A case study[J].Applied radiation and isotopes: including data, instrumentation and methods for use in agriculture, industry and medicine,2007(1):131-141. |
| [4] | Sunil Kumar .Fly ash-lime-phosphogypsum hollow blocks for walls and partitions[J].Building and environment,2003(2):291-295. |
| [5] | Ambarish Ghosh .Compaction Characteristics and Bearing Ratio of Pond Ash Stabilized with Lime and Phosphogypsum[J].Journal of Materials in Civil Engineering,2010(4):343-351. |
| [6] | Manjit Singh .Treating waste phosphogypsum for cement and plaster manufacture[J].Cement and Concrete Research,2002(7):1033-1038. |
| [7] | 张毅,王小鹏,李东旭.大掺量工业废石膏制备石膏基胶凝材料的性能研究[J].硅酸盐通报,2011(02):367-372. |
| [8] | 杨家宽,谢永中,刘万超,任婷艳,林显龙.磷石膏蒸压砖制备工艺及强度机理研究[J].建筑材料学报,2009(03):352-355. |
| [9] | 吴其胜,刘学军,黎水平,叶菁华,张长森.脱硫石膏-矿渣微粉复合胶凝材料的研究[J].硅酸盐通报,2011(06):1454-1458. |
| [10] | Edinger S E .An investigation of the factors which affect the size and growth of the habit faces of gypsum[J].Journal of Crystal Growth,1973,13(03):217. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%