采用原位矿化复合-固相挤出技术制备羟基磷灰石/高密度聚乙烯(HA/HDPE)复合材料.结果表明,原位矿化-固相挤出制备的HA/HDPE复合材料是一种纳米HA颗粒均匀分散、界面结合强度高、HA/HDPE复合纤维定向排列的多尺度结构复合材料,在纳米尺度上HA均匀分散在HDPE基体中,在微米尺度上形成HA/HDPE复合纤维,在显微尺度上定向排列的HA/HDPE复合纤维形成织构结构.该HA/HDPE多尺度结构复合材料的力学性能与传统的熔融挤出的HA/HDPE复合材料相比有显著提高,拉伸强度达到245 Mpa,弯曲强度达到165 Mpa,拉伸模量为18.1 Gpa,力学性能均达到人体皮质骨的力学要求.