为了提高铝材的耐蚀性和表面硬度,用柠檬酸体系在铝基体上制备了Ni-Cr合金镀层.研究了工艺参数对镀层组成、形貌和结构的影响,确定了最佳工艺条件.结果表明:最佳工艺条件获得的镀层光亮、平滑,显示出密集的球形细粒状形貌特征;镀层为面心立方(FCC)Ni-Cr固溶体纳米晶结构;适当降低温度,增大电流密度,提高镀液中CrCl3浓度,有利于镀层表面合金颗粒细化和晶体粒径的减小,晶体结构有序性增强;随着pH值升高,镀层颗粒细化,晶型改善,当pH值大于3时,镀层晶体粒径逐渐变粗,内应力增大,表面形貌变差.随着Cr含量增大,镀层表面粒径减小,晶界延长,镀层耐蚀性提高;镀层与Al基体结合良好.
参考文献
| [1] | A. BOUYAGHROUMNI;P. VERSAUD;O. VITTORI .ELECTRODEPOSITION OF Co-Ni ON ALUMINUM PLATE FROM CHLORIDE BATH[J].Canadian Metallurgical Quarterly,1996(3):245-253. |
| [2] | M. H. Pournaghi-Azar;H. Razmi-Nerbin .Voltammetric behaviour and electrocatalytic activity of the aluminum electrode modified with nickel and nickel hexacyanoferrate films, prepared by electroless deposition[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,1998(1/2):83-90. |
| [3] | 宋博,张学枕,牛桂英,刘慎中,隋智通.铝合金基体电沉积镍层结合强度的研究[J].长春理工大学学报,2002(04):57-60. |
| [4] | 周崎,张安富,李国洪.铝合金直接电镀镍工艺的研究[J].材料保护,2002(06):25-26. |
| [5] | 马洪芳,刘志宝,殷风玲.铝合金电镀工艺研究[J].腐蚀与防护,2003(04):162-163. |
| [6] | 丁雨田,许广济,戴雷,尹建军,寇生中,喇培清.铝合金表面电沉积Ni-SiC复合镀层的研究[J].机械工程学报,2003(01):128-132. |
| [7] | Wang DQ;Shi ZY;Kou TS .Composite plating of hard chromium on aluminum substrate[J].Surface & Coatings Technology,2005(2/3):324-329. |
| [8] | YANG Yu-fang,GONG Zhu-qing,DENG Li-yuan,LUO Bei-ping,MA Yu-tian,YANG Zhen-hui.Electrodeposition of Ni-Cr alloy on aluminum substrate[J].中南工业大学学报（英文版）,2006(03):219-224. |
| [9] | 杨余芳,龚竹青,罗娟,马玉天,阳征会.Ni-Cr合金在三价铬水溶液中的电沉积[J].材料保护,2006(06):21-25. |
| [10] | 杨余芳,李强国.Ni-Cr合金共沉积的电化学特性[J].材料保护,2008(05):15-18,25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%