采用矩形剥离缝隙模型,原位测量了酸性鹰潭土壤模拟溶液中的剥离区滞留液的成分变化,选配了剥离体系腐蚀前期和后期的模拟滞留液溶液,并通过动电位极化曲线、电化学阻抗谱和微观形貌分析对其腐蚀性进行评价.结果表明,剥离体系腐蚀后期滞留液的C1-,Na+,K+含量升高,溶解氧含量减少、pH降低,其腐蚀电流密度升高,电荷转移电阻Rct减小,保护性腐蚀产物膜受到破坏,点蚀程度明显加重.相较本体溶液和前期滞留液,后期滞留液的腐性更严重.
参考文献
| [1] | Flavio Deflorian;Stefano Rossi .An EIS study of ion diffusion through organic coatings[J].Electrochimica Acta,2006(8/9):1736-1744. |
| [2] | Chin D.T.;Sabde G.M. .Modeling Transport Process and Current Distribution in a Cathodically Protected Crevice[J].Corrosion: The Journal of Science and Engineering,2000(8):783-793. |
| [3] | 刘智勇,董超芳,贾志军,李晓刚.X70钢在模拟潮湿存储环境中的点蚀行为[J].金属学报,2011(08):1009-1016. |
| [4] | Local additional potential model for effect of strain rate on SCC of pipeline steel in an acidic soil solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(12):2863. |
| [5] | Huichao Bi;John Sykes .Cathodic disbonding of an unpigmented epoxy coating on mild steel under semi- and full-immersion conditions[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(10):3416-3425. |
| [6] | Rongguang Wang .Influence of ultrasound on pitting corrosion and crevice corrosion of SUS304 stainless steel in chloride sodium aqueous solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(2):325-328. |
| [7] | X. He;D. S. Dunn;A. A. Csontos .Corrosion of similar and dissimilar metal crevices in the engineered barrier system of a potential nuclear waste repository[J].Electrochimica Acta,2007(27):7556-7569. |
| [8] | Effect of cathodic protection on corrosion of pipeline steel under disbonded coating[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(9):2242. |
| [9] | Han, D.;Jiang, Y.M.;Shi, C.;Deng, B.;Li, J. .Effect of temperature, chloride ion and pH on the crevice corrosion behavior of SAF 2205 duplex stainless steel in chloride solutions[J].Journal of Materials Science,2012(2):1018-1025. |
| [10] | 陈旭,李晓刚,杜翠薇,梁平.阴极极化条件下X70钢的缝隙腐蚀行为[J].金属学报,2008(12):1431-1438. |
| [11] | M. Z. Yang;M. Wilmott;J. L. Luo .Crevice corrosion behavior of A516-70 carbon steel in solutions containing inhibitors and chloride ions[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1998(1/2):180-188. |
| [12] | 杨佳星,赵平,孙成,许进.埋地管线钢缝隙腐蚀的机理与防护研究进展[J].全面腐蚀控制,2010(04):16-19,10. |
| [13] | 刘智勇,李晓刚,杜翠薇,陈旭,梁平,张亮.管道钢在土壤环境中应力腐蚀模拟溶液进展[J].油气储运,2008(04):34-39. |
| [14] | 李正奉,毛旭辉,甘复兴.阴极保护下缝隙内的电流分布[J].中国腐蚀与防护学报,2000(06):338-242. |
| [15] | A. M. Al-Zahrani;H. W. Pickering .IR voltage switch in delayed crevice corrosion and active peak formation detected using a repassivation-type scan[J].Electrochimica Acta,2005(16/17):3420-3435. |
| [16] | 宋义全,杜翠薇,张新,李晓刚.Cl-浓度对X70管线钢缝隙腐蚀的影响[J].金属学报,2009(09):1130-1134. |
| [17] | 陈旭,杜翠薇,梁平,李晓刚.酸性土壤环境中X70钢缝隙腐蚀行为的研究[J].科学通报,2008(23):2839-2847. |
| [18] | A.Q. Fu;X. Tang;Y.F. Cheng .Characterization Of Corrosion Of X70 Pipeline Steel In Thin Electrolyte Layer Under Disbonded Coating By Scanning Kelvin Probe[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(1):186-190. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%