将聚丙烯腈碳纤维毡在450－650℃下于空气中恒温处理2h，采用扫描电镜、拉曼光谱仪、电阻仪等研究了热处理温度对碳纤维毡的表面形态、结构、导电性能的影响。结果表明：随着热处理温度的升高，碳纤维毡表面存在的杂质逐渐分解消失，并出现空洞、沟槽等缺陷，碳纤维结构逐渐从二维的乱层结构转变为三维的有序结构；碳纤维毡的电导率先升后降，在550℃时达到最大值。
The polyacrylonitrile carbon felt was heated for 2 hours at 450--650 ℃ in air, respectively. The effect of heat-treatment temperature on surface state, structure and conductivity of the carbon felt were studied by scanning electron microscopy (SEM), Raman spectroscopy and resistance meter. The results show that the impurities' gradually disappeared and some defects, such as holes and grooves, appeared with the increase of the heat treatment temperature. The structure of carbon fiber gradually changed from planar turbostratie structure to three dimensional ordered structure. The conductivity of carbon felt raised and then decreased, and reached the maximum at 550 ℃.
参考文献
| [1] | 岳鹿,李伟善.热处理碳纸的氧化过程及其对钒离子的电催化[J].电源技术,2010(12):1262-1265. |
| [2] | 周蔚虹,张红波,刘洪波.毡体热处理对炭/炭复合材料氧化行为的影响[J].炭素,2003(04):19-22. |
| [3] | 刘素琴,郭小义,黄可龙,刘勇刚,李晓刚.钒电池电极材料聚丙烯腈石墨毡的研究[J].电池,2005(03):183-184. |
| [4] | 史小虎 .全钒液流电池电极材料的改性及电池结构的组装优化[D].中南大学,2009. |
| [5] | 靳玉伟,刘钟铃,高爱君,徐翊桄,徐樑华.热处理对PAN基碳纤维结构与性能的影响[J].合成纤维工业,2010(05):1-4. |
| [6] | Cedric Sauder;Jacques Lamon;Rene Pailler .The tensile behavior of carbon fibers at high temperatures up to 2400 deg C[J].Carbon: An International Journal Sponsored by the American Carbon Society,2004(4):715-725. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%