采用激光熔覆原位合成技术在不锈钢基体表面制备了TiB2/WC增强镍基复合涂层,用X射线衍射仪、能谱仪、扫描电镜等对涂层进行了分析,并对涂层进行了热震试验.结果表明:涂层致密、厚度均匀、表面平整、无裂纹和孔隙、与基体呈冶金结合;涂层主要由TiB2、WC、γ-Ni等物相组成,细小的TiB2和WC粒子主要分布于γ-Ni枝晶间,可阻碍基体晶粒晶界的推移长大;WC 颗粒主要分布于涂层中部和下部区域,原位合成的细小TiB2粒子主要分布于涂层上部;涂层具有较高的抗裂能力,与基体具有良好的结合强度.
参考文献
[1] | S. Barnes;N. Timms;B. Bryden .High power diode laser cladding[J].Journal of Materials Processing Technology,2003(1/3):411-416. |
[2] | Conde A.;Zubiri F.;de Damborenea J. .Cladding of Ni-Cr-B-Si coatings with a high power diode laser[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):233-238. |
[3] | Yang S.;Zhong ML.;Liu WJ. .TiC particulate composite coating produced in situ by laser cladding[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):57-62. |
[4] | 孙荣禄,杨贤金.激光熔覆原位合成TiC-TiB2/Ni基金属陶瓷涂层的组织和摩擦磨损性能[J].硅酸盐学报,2003(12):1221-1224. |
[5] | 袁晓敏,龚佑品,何宜柱.TiB2对Ni基合金激光熔覆层组织与性能的影响[J].焊接学报,2007(05):41-44. |
[6] | 张维平,刘硕.激光熔覆原位生成TiB2热力学及动力学分析[J].材料科学与工程学报,2004(05):701-704. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%