应用扫描电镜原位拉伸的方法和有限元法研究了Al单晶在不同Ⅰ+Ⅱ型复合载荷下裂纹尖端变形损伤行为和裂端的变形场、约束场.实验结果表明:①复合裂端变形是钝一锐化模型,钝锐化分别由均匀滑移和集中滑移控制;②复合损伤及断裂是均匀滑移的结果,裂纹沿裂端最大约束的方向扩张;③随H型分量的增加,裂纹启裂的COD值增加;@各复合比下裂端启裂等效应变εf与最大裂端约束R
An in-situ tensile experiment in a SEM and finite element method have been made into the deformation and damage behaviors, the strain and restrain fields at the crack tip under the different Ⅰ+Ⅱmixed mode ratios in an Al single crystal.The results show th
参考文献
| [1] | .S.M.Ohr, Mater.Sci. Eng. 72(1),1(1985) |
| [2] | .S.M.Ohr, Scr Met. 20(9), 1501(1986) |
| [3] | .史耀武JTVarnby,金属学报,20,A17(1984) |
| [4] | .姚可夫,唐迪泳,南平.金属学报,27(6),A395(1991) |
| [5] | .V.Tvergaard,1 Mech. Phys. Solids, 35(2), 151(1987) |
| [6] | .V.Tvergaard, Int.J Solids Struct 18(7), 659(1982 |
| [7] | .沙江波.复合型弹性塑性损伤断裂机理及准则的研究,博士学位论文,西安交通大学(1994) |
| [8] | .N.T.Tang, K.F.Yao and A.Plumtree, Mater. Set. Eng, 8(3), 245(1992) |
| [9] | .郑长卿,张克实,岳珠峰,周利.裂纹体与无裂纹体统一损伤断裂理论研究文集.(西北工业大学出版社,西安,1991)p.69 |
| [10] | .C.F、Shih, ASTM STP, 560(1974) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%