研究了不同热处理工艺对一种镍基单晶高温合金的组织和持久性能的影响.结果表明:固溶处理时间越长,合金中的γ'相尺寸越均匀,有利于合金持久性能的提高.1080℃,4 h和1150℃,4 h时效后空冷获得的y'相具有尺寸适合、立方度高的特点.2种时效处理对合金中温高应力的持久性能影响不明显,在高温低应力下,经1080℃时效处理的持久寿命略长.
参考文献
| [1] | Reichman S.Superalloys 1988[M].New York:The Metallurgical Society,1988:245. |
| [2] | Diologent F;Caron P .On the creep behavior at 1033 K of new generation single-crystal superalloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):245-257. |
| [3] | Murakumo T et al.[J].Acta Materialia,2004,52:3737. |
| [4] | Caron P et al.[J].Scripta Materialia,1986,20:875. |
| [5] | MacKay R A et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16:1969. |
| [6] | Allen S.[A].Ohio:ASM,1986:41. |
| [7] | 刘丽荣,金涛,赵乃仁,王志辉,孙晓峰,管恒荣,胡壮麒.一种Ni基单晶高温合金[001]方向的持久性能与断裂行为[J].金属学报,2004(08):858-862. |
| [8] | 任英磊,金涛,管恒荣,胡壮麒.固溶处理对1种镍基单晶高温合金组织的影响[J].稀有金属材料与工程,2003(04):287-290. |
| [9] | 刘丽荣.[J].材料工程,2002:112. |
| [10] | Tien J K.Metal Progres[M].London:Academic Press,1989:149. |
| [11] | Tien J K.[A].OH:USA,1980:513. |
| [12] | Caron P et al.[J].Materials Science and Engineering,1983,61:173. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%