通过六氯环三磷腈的热开环聚合合成了线性聚二氯磷腈(PDCP)中间体,探讨了聚合时间、聚合温度单体纯度及空气湿度等对PDCP合成的影响,采用FT-IR、TGA对PDCP进行了表征.TGA结果表明,PDCP呈现明显的二段降解性;通过正丁醇对PDCP进行亲核取代合成了聚双正丁氧基磷腈,采用FT-IR、TGA、SEM对聚双正丁氧基磷腈进行了表征,TGA结果表明,聚双正丁氧基磷腈具有优良的热稳定性和较高的残留率,SEM结果表明,材料形貌呈现无定形态分布,而且其表面比较光滑无明显缺陷.
参考文献
| [1] | Allcock H R;Kugel R L .Synthesis of high polymeric alkoxy and arylozyphosphonitriles[J].Journal of the American Chemical Society,1965,87:4216. |
| [2] | Harry R Allcock .Recent developments in polyphosphazene materials science[J].Current Opinion in Solid State and Materials Science,2006,10:231. |
| [3] | Martin Breza .On the structure of polyphosphazenes[J].European Polymer Journal,1999(4):581-586. |
| [4] | Paulsdorf J;Burjanadze M;Hagelschur K;Wiemhofer HD .Ionic conductivity in polyphosphazene polymer electrolytes prepared by the living cationic polymerization[J].Solid state ionics,2004(1/4):25-33. |
| [5] | Harry R Allcock;E Clay Kellam Ⅲ .The synthesis and applications of novel aryloxy/oligo ethyleneoxy substituted polyphosphazenes as solid polymer electrolytes[J].Solid State Ionics,2003,156:401. |
| [6] | Allcock H R;Laurencin C T .Preparation of poly[bis(carboxylatophenoxy)] phosphazene non-woven nanofiber mats by electrospinning[J].Proc Mater Res Soc,2004,8(10):157. |
| [7] | 徐师兵.芳氧基取代聚磷腈的合成与表征[J].吉林大学自然科学学报,1994(04):104-108. |
| [8] | 任杰,陈云华.聚磷腈的研究和应用[J].材料导报,2004(07):58-61. |
| [9] | 李爱元,张慧波,陈亚东,王建中,储昭荣.聚磷腈在航空航天高分子材料中的应用[J].化学推进剂与高分子材料,2007(06):40-44. |
| [10] | 刘元 .氟代烷氧基取代聚磷腈类高性能弹性体的基础性研究[D].北京:北京化工大学,2007. |
| [11] | 李振,詹才茂,秦金贵.聚磷腈高分子[J].功能高分子学报,2000(02):240-246. |
| [12] | 戈丹 .聚磷腈的合成及其表面性能[D].杭州:浙江大学,2007. |
| [13] | 刘朋军,张连华.聚磷腈功能材料研究进展[J].化学研究与应用,2001(01):33-38,封3. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%