以纯W粉末为熔覆材料,纯Ta为基底,采用同轴送粉激光熔覆技术在Ta板侧面制备了Ta-W合金涂层.利用扫描电镜(SEM)、能谱(EDS)及显微硬度计对熔覆层的微观组织和显微硬度进行了分析,在直联式自由射流风洞试验台上对涂层的抗高温高速气流烧蚀性能进行了测试.结果表明,熔覆层与基底冶金结合,涂层内部为致密的树枝状Ta-W合金固溶体,大致均匀地分布于Ta中.TaW合金涂层平均HV硬度8 GPa,为基材的5倍,同时抗烧蚀性能得到了显著提高.
参考文献
| [1] | Etemad G A .[J].AIAA Journal,1966,4(09):1543. |
| [2] | White J E .[J].AIAA Journal,1966,4(02):307. |
| [3] | Marshall B W .[J].AIAA Journal,1966,4(11):1899. |
| [4] | ZHOU Jian-qiu,Akhtar S. Khan,CAI Rui,CHEN Ling.Comparative Study on Constitutive Modeling of Tantalum and Tantalum Tungsten Alloy[J].钢铁研究学报（英文版）,2006(04):68-74. |
| [5] | Byun TS;Maloy SA .Dose dependence of mechanical properties in tantalum and tantalum alloys after low temperature irradiation[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2008(1):72-79. |
| [6] | 张廷杰;张德尧;丁旭 .[J].稀有金属材料与工程,1996,25(04):5. |
| [7] | 吴孟海,李树清,许德美,赵洪章.Ta-10W合金的高温力学性能[J].稀有金属材料与工程,2006(z2):64-67. |
| [8] | Mazumder J.;Kikuchi N.;Ghosh A.;Dutta D. .Closed loop direct metal deposition: art to part[J].Optics and Lasers in Engineering,2000(4/6):397-414. |
| [9] | 钟如涛,熊征.连续/脉冲C02激光熔覆高温合金K403[J].中国激光,2010(03):852-857. |
| [10] | 王晶,宋仁国,林鑫,黄卫东.γ-TiAl金属间化合物合金表面激光熔覆TiC-Ti-Al涂层研究[J].稀有金属材料与工程,2008(12):2191-2195. |
| [11] | 王宏宇,左敦稳,王明娣,邵建兵.纳米CeO2p对镍基高温合金表面NiCoCrAlY激光熔覆涂层氧化行为的影响[J].金属学报,2009(08):971-977. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%