采用金相显微镜、电子能谱分析仪、透射电子显微镜、FeCl3溶液浸泡法和循环极化曲线法研究了固溶处理对2205双相不锈钢组织和点腐蚀性能的影响.结果表明,经1050℃×2h水冷固溶处理后,实验钢中α和γ两相体积含量约各占一半,组织均匀且细化,在6%FeCl3,溶液中的临界点蚀温度为45℃,在3.5%NaCl溶液中的点蚀电位Eb和保护电位Ep均为1028mV,表现出良好的耐点蚀性能.经950℃固溶处理后组织中析出σ相,σ相导致其抗点蚀性能下降.
参考文献
| [1] | M. Oberndorfer;K. Thayer;M. Kastenbauer .Application limits of stainless steels in the petroleum industry[J].Materials and Corrosion,2004(3):174-180. |
| [2] | Madsen A C;Mueller F O;Geisort R et al.Duplex stainless steel pipelines and piping on the north slope[J].Materials Performance,1987,26(02):49-55. |
| [3] | 陈彰兵,宋德琦,汤晓勇,张强.双相不锈钢在克拉2气田中的应用[J].天然气与石油,2006(03):1-6,11. |
| [4] | Walden B;Nicholls J M .Physieal metallurgy and some characteristic properties of the Sandvik duplex stainless steels[Sandvik Steel Report,S-51-54-ENG][R].,1994. |
| [5] | Potgieter J H .Influence of σphase on general and pitting corrosion resistance of SAF 2205 duplex stainless steel[J].British Corrosion Journal,1992,27(03):219-224. |
| [6] | 秦紫瑞;郭宁;郭珊 等.耐"NaClO+NaCl"复合介质新型双相不锈钢的研究[J].腐蚀与防护,1996,18(02):60-64. |
| [7] | 路新春;李诗卓;张天成 等.固溶处理温度对双相不锈钢在硫酸介质中腐蚀磨损行为的影响[J].金属学报,1994,30(04):159-164. |
| [8] | 吴玖.双相不锈钢[M].北京:冶金工业出版社,1996:124-125. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%