采用大型真空镀膜设备在玻璃基底上蒸镀二氧化钛(TiO2)薄膜,并对TiO2薄膜进行了SEM、AFM、XRD、紫外可见光吸收光谱、亲水性的测试及分析,探讨了退火温度对薄膜性能的影响.结果表明制备的TiO2薄膜具有良好的均匀性.在室温条件下,TiO2薄膜具有无定型的结构;在300～500℃的条件下,TiO2薄膜退火2h后以锐铁矿晶型为主,600℃退火的TiO2薄膜明显向金红石型转变.随退火温度的升高,薄膜对紫外光和可见光的吸收有明显提高,并出现了明显的红移现象.另外,亲水性也随退火温度的升高而变强,500和600℃退火的TiO2薄膜表面出现超亲水性.
参考文献
| [1] | Fujishima A;Honda K .[J].Nature,1972,238(01):37-40. |
| [2] | Carey J H;Lawrence J;Tosine H M .[J].Bulletin of Environmental Contamination and Toxicology,1976,16:697-701. |
| [3] | Wang R;Hashimoto K;Fujishima A et al.[J].Nature,1997,388:431-432. |
| [4] | Yu J G;Zhao X J .[J].Chemical Research in Chinese Universities,2000,21(09):1437-1440. |
| [5] | Carp O;Huisman C L et al.[J].Progress in Solid State Chemistry,2004,32(1-2):33-36. |
| [6] | Mills A;Lepre A;Elliott N et al.[J].Journal of Photochemistry and Photobiology A:Chemistry,2003,160:213-224. |
| [7] | Watarmbe T .[J].Bulletin Ceramic Society of Japan,1996,31(10):837-840. |
| [8] | 刘敬肖,杨大智,蔡英骥.溶胶-凝胶法制备TiO2与SiO2-TiO2薄膜对医用NiTi合金的表面改性[J].材料研究学报,2002(05):523-528. |
| [9] | Zhai J W;Zhang L Y;Yao X .[J].J lnor Mater,1999,14(01):133-137. |
| [10] | Zhu L J;Cui Y M .[J].Journal of Materials Science and Technology,2007,15(06):876-880. |
| [11] | Peng X G;Wang Y .[J].Materials Review,2008,22(01):5-8. |
| [12] | Xiao Y F;Liu S .[J].Bull Chin Cera Soc,2007,26(03):523-528. |
| [13] | 宋林云,吴玉程,李云,叶敏,解挺,黄新民,郑治祥.介孔Co-TiO2的制备及其光催化性能研究[J].功能材料,2008(01):32-35. |
| [14] | 林志东,刘黎明.AFM分析磁控溅射法制备的TiO2纳米薄膜[J].武汉化工学院学报,2005(01):52-55. |
| [15] | Liu P Y;Ye Q;Tang Z F et al.[J].Vacu Sci Tech,2004,24(02):133-136. |
| [16] | Loddo V;Marci G;Martin C et al.[J].Applied Catalysis B:Environmental,1999,20:29-35. |
| [17] | Lu G Q;Linsebigler A;John T et al.[J].Journal of Physical Chemistry,1994,98:11733-11738. |
| [18] | Fujishima A;Rao T N;Tryk D A .[J].Journal of Photochemistry and Photobiology C:Photochemistry Reviews,2000,1:1-21. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%