为了解结晶器与坯壳间渣膜的结晶状态,用热丝法熔化性能测定仪对保护渣结晶性能进行研究.结果表明:连续冷却过程中,结晶是在一定温度范围内进行的;冷却速率越大,结晶温度越低;冷却速率超过一定值时,保护渣不结晶.不同温度下的等温实验结果表明:在一定过冷度范围内,保护渣开始结晶; 过冷度的大小与结晶开始和结束时间有关;水蒸气可促进保护渣结晶,在不同温度等温时,保护渣结晶开始温度提高,结晶开始时间缩短.
参考文献
| [1] | 申俊峰;庞智杰 .结晶器保护渣渣膜的研究[J].炼钢,1998,14(04):31-33. |
| [2] | Masayuki Kawamoto;Keiji Nakajima .Development of MildCooling Mold Powder for Peritectic Steel Slab[J].CAMP-ISIJ,1993,6:283. |
| [3] | Hiroyuki SHIBATA;Toshihiko EMI .Thermal Diffusivities of Continuous Casting Mold Fluxes for Steel in the Glassy and Crystalline States[J].鉄と鋼,1996(6):46-50. |
| [4] | Raman S;Sankaranrayaman D A.The Analysing and Evalua-ting of Mold Flux Properties by Crystallization[A].Washington:Iron and SteelSociety,1991:167-178. |
| [5] | EMLING W H .Breakout Prevention[J].Ironmaking and Steelmaking,1994,21(05):50-51. |
| [6] | C.A. Pinheiro;I.V. Samarasekera;J.K. Brimacombe .Mold Flux for Continuous Casting of Steel[J].Iron & Steelmaker,1996(3):85-0. |
| [7] | C.A. Pinheiro;I.V. Samarasekera;J.K. Brimacombe .Mold Flux for Continuous Casting of Steel[J].Iron & Steelmaker,1996(1):51-52. |
| [8] | Yoshiaki Kashiwaya;Cicutti C E;Cramb A W .Investigationof the Crystallization of a Continuous Casting Mold Slag Usingthe Single Hot Thermolcouple Technique[J].ISIJ International,1998,38(04):348-356. |
| [9] | 刘智恩.材料科学基础[M].西安:西北工业大学出版社,2000 |
| [10] | 迟景灏;甘永年.连铸保护渣[M].沈阳:东北大学出版社,1993 |