采用气电立焊及热模拟试验研究了原油储罐用高强钢大热输入焊后热影响区、尤其是粗晶热影响区的组织与性能.结果表明,TMCP高强钢大热输入焊后粗晶区组织粗大,以板条贝氏体为主,距熔合线0.5 mm处冲击吸收功最低(77 J),冲击值完全高于标准要求(47 J).Nb0.026％ TMCP钢热影响区中导致冲击韧性严重下降的脆性M-A组元含量极少,这与钢中固溶的Nb含量较少有关,固溶Nb能降低γ-α转变温度,促使粒状贝氏体形成;Nb0.014％ RQ+T钢降低了Nb含量,同时添加少量Ti,形成Ti、Nb复合添加,热影响区M-A组元含量很少,冲击韧性接近TMCP钢.
参考文献
| [1] | Chiaki OUCHI .Development of Steel Plates by Intensive Use of TMCP and Direct Quenching Processes[J].ISIJ International,2001(6):542-553. |
| [2] | Nishioka K;Ichikawa K .Progress in thermomechanical control of steel plates and their commercialization[J].SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS,2012,13(2):1-20. |
| [3] | A. J. DeArdo .Niobium in modern steels[J].International Materials Reviews,2003(6):371-402. |
| [4] | 刘振伟,郭晖,尚成嘉,付彦0,王晓香,缪成亮.Nb含量和热输入量对X80管线钢焊接粗晶区的影响[J].材料热处理学报,2012(01):99-105. |
| [5] | 张英乔,张汉谦,赵四新,刘伟明.铌对高强结构钢大热输入焊接热影响区组织和性能的影响[J].焊接学报,2008(09):96-100. |
| [6] | B.Meester .The Weldability of Modern Structural TMCP Steels[J].ISIJ International,1997(6):537-542. |
| [7] | 贾坤宁,姜秋月,王敏.高强度桥梁钢焊接粗晶热影响区中粒状贝氏体对韧性的影响[J].金属热处理,2011(12):41-43. |
| [8] | 王小勇,潘涛,苏航,李向阳.Ni-Cr-Mo-B低合金钢模拟焊接热影响区的组织和性能[J].材料热处理学报,2012(08):69-73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%