The chemical composition and mineral structure of fluorgypsum as well as its harm to application in cement were elaborately analyzed. The primary fluorgypsum was modified and its applications in cement's production were studied. The technological flow chart of preparing modified fluorgypsum was given.Experimental results indicate that hydration ratio the modified fluorgypsum through adding compound additive for 14d is about 70%. The modified fluorgypsum as cement retarder has certain stimulation to fly ash and increases the strength of compound cement. In addition, its adding amount is lower than that of natural gypsum.The modified fluorgypsum is a good substitute for natural gypsum.
参考文献
| [1] | Xu Qing.Comprehensive Utilization Discussion on Fluorine Gypsum of Fluorid Salt Factory[J].Journal of Light Metals,2000(10):12-15. |
| [2] | Zhu Xiaoli;Yang Xiaowen.Experiment on Using Fluorine Gypsum as Retarder Instead of Natural Gypsum[J].Journal of Tangshan Polytechnic College,1999(04):29-31. |
| [3] | 田京城.氟石膏的综合利用现状与展望[J].徐州工程学院学报,2005(01):104-107. |
| [4] | 阎培渝,游轶.在不同条件养护的氟石膏粉煤灰胶结材的水化硬化性能[J].硅酸盐学报,1998(06):689-694. |
| [5] | 许红升,张锦峰,李国忠.复合外加剂对氟石膏制品强度和泛霜效果影响的研究[J].墙材革新与建筑节能,2005(11):32-34. |
| [6] | Yang Xinya;Wang Jinhua .Recycling Modification Method of Fluorin Gypsum[P].CN 200410013136.2,2006. |
| [7] | Chen Yan;Yue Wenhai;Dong Ruolan.Gypsum Building Material[M].北京:中国建筑工业出版社,2002:192. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%