以钢渣和粉煤灰为主要原料,加入一定的无烟煤熔融还原后采用烧结法制备微晶玻璃,并采用XRD、SEM等手段研究了晶化温度和成型压力对钢渣基微晶玻璃性能的影响.结果表明,随着晶化温度的增加,钙铝黄长石的衍射峰强度先增强后减弱,当晶化温度为867℃时,其衍射峰强度最强,晶体发育较好,分布均匀致密且试样的显微硬度和抗压强度最佳;在其基础上素坯采用30 MPa的成型压力后,烧制后的微晶玻璃晶粒尺寸为1～2 μm左右,其抗弯强度为63.59 MPa,抗压强度为313.91MPa.
参考文献
| [1] | 刘文丽,杜晓玮.浅谈钢渣的综合利用途径[J].能源与节能,2011(04):55-57,94. |
| [2] | 封鉴秋,谭伟,李素平,郑艳.钢渣-粉煤灰微晶玻璃的研制[J].河南建材,2010(06):40-42. |
| [3] | 李保卫,杜永胜,张雪峰,贾晓琳,陈华,赵鸣,邓磊波.基础成分配比对白云鄂博尾矿微晶玻璃结构及性能的影响[J].人工晶体学报,2012(05):1391-1398. |
| [4] | 王琳,孙本良,李成威.钢渣处理与综合利用[J].冶金能源,2007(04):54-57. |
| [5] | 陈维铅,高淑雅,刘杰,董亚琼.熔融法制备金尾矿微晶玻璃及性能研究[J].人工晶体学报,2014(01):217-221. |
| [6] | 王艺慈,于文武,张建良,罗果萍,姜祺.包钢高炉渣微晶玻璃的析晶动力学及显微结构分析[J].材料热处理学报,2014(01):88-93. |
| [7] | Fredericci C;Pizani PS;Morelli MR .Crystallization of blast furnace slag glass melted in SnO2 crucible[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2007(44/46):4062-4065. |
| [8] | 陈左朋,申星梅,吕辉鸿,李辽沙.风淬钢渣对高炉渣基微晶玻璃性能的影响[J].环境工程学报,2013(02):732-736. |
| [9] | 田清波,孔德钰,代金山,王修慧,高宏.SiO2-Al2O3-MgO-F系微晶玻璃的受压析晶[J].人工晶体学报,2014(02):409-413. |
| [10] | 杜永胜,李保卫,张雪峰,贾晓琳,陈华,赵鸣,邓磊波.铁含量及价态对白云鄂博尾矿微晶玻璃析晶特性及性能的影响[J].人工晶体学报,2013(10):2170-2176. |
| [11] | Duan, F. .Effects of CaO on crystallization properties in BaO-SrO-TiO _2-SiO_2 glass-ceramics[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2011(5):1494-1497. |
| [12] | 周曦亚,胡俊,周斌扬,刘林凤.CaF_2含量对CaO-SiO_2-R_2O-F系微晶玻璃晶化行为的影响[J].硅酸盐通报,2009(05):1024-1028. |
| [13] | RITWIK SARKAR;NAR SINGH;SWAP AN KUMAR DAS .Utilization of steel melting electric arc furnace slag for development of vitreous ceramic tiles[J].Bulletin of Materials Science,2010(3):293-298. |
| [14] | Yan Zhao;Dengfu Chen;Yanyan Bi .Preparation of low cost glass-ceramics from molten blast furnace slag[J].CERAMICS INTERNATIONAL,2012(3):2495-2500. |
| [15] | 曹超,彭同江,丁文金.晶化温度对CaO-Al2O3-SiO2-Fe2O3系粉煤灰微晶玻璃析晶及性能的影响[J].硅酸盐学报,2013(01):122-128. |
| [16] | 张凯,武文斐,杨家宽.晶化温度对热态钢渣基微晶玻璃结构和性能的影响[J].武汉理工大学学报,2013(09):36-39. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%