采用热压烧结工艺制备了AlN-SiC复相陶瓷材料,用XRD、SEM和激光导热仪等研究了SiC加入量和烧结温度对复相陶瓷材料导热性能的影响.结果表明:当质量分数在20%～75%范围内,随着SiC含量的增加,复相陶瓷材料的热导率逐渐增大,最大热导率达到了88.92 W·m-1·K-1;进一步增加SiC的含量,复相材料的热导率又呈现下降趋势,当SiC质量分数为80%时,热导率降到了42.70 W·m-1·K-1;当SiC质量分数为20%时,随着烧结温度的升高(1 800～1 950℃),复相陶瓷材料的热导率逐渐上升,从42.15 W·m-1·K-1增加到68.41 W·m-1·K-1.
参考文献
| [1] | Huang JL.;Jih JM. .INVESTIGATION OF SIC-ALN .2. MECHANICAL PROPERTIES[J].Journal of the American Ceramic Society,1996(5):1262-1264. |
| [2] | Young-Wook Kim;Mamoru Mitomo;Toshiyuki Nishimura .High-Temperature Strength of Liquid-Phase-Sintered SiC with AIN and Re_2O_3 (RE=Y, Yb)[J].Journal of the American Ceramic Society,2002(4):1007-1009. |
| [3] | Diletta Sciti;Stefano Guicciardi;Cesare Melandri .High-Temperature Resistant Composites in the AlN-SiC-MoSi_2 System[J].Journal of the American Ceramic Society,2003(10):1720-1726. |
| [4] | 高陇桥.大功率真空电子器件实用的高热导率陶瓷的进展[J].真空电子技术,1999(02):27. |
| [5] | Inger-Lise Tangen;Yingda Yu;Tor Grande .Preparation and characterisation of aluminium nitride-silicon carbide composites[J].Ceramics International,2004(6):931-938. |
| [6] | 郑永挺,赫晓东,曲伟,张学忠.Y2O3对氮化铝陶瓷燃烧合成致密化及组织性能的影响[J].哈尔滨工业大学学报,2002(04):483-488. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%