采用水雾化法制备了纳米晶Fe85.Si9.6 Al5.4(wt.%)抗电磁干扰软磁合金粉末,研究不同工艺参数对其扁平度的影响.研究发现,在球磨过程中添加正己烷作为辅助剂,可以有效获得高扁平度粉末.对于不同直径的球磨球,当球料比为5:1时,获得最大扁平度的球磨时间不同.本文研究结果对实现Fe-Si-A1合金在高频下的应用具有一定的指导意义.
参考文献
| [1] | R. M. Walser;Wooseung Kang .Fabrication and properties of microforged ferromagnetic nanoflakes[J].IEEE Transactions on Magnetics,1998(4 Pt.1):1144-1146. |
| [2] | A.H. Kasama;C. Bolfarini;C.S. Kiminami;W.J. Botta Filho .Magnetic properties evaluation of spray formed and rolled Fe-6.5 wt.% Si-1.0 wt.% Al alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):375-377. |
| [3] | 邓联文,冯则坤,江建军,何华辉,付祺伟,熊惟皓.纳米晶Fe85Si1Al6Cr8扁平状颗粒材料微波吸收特性[J].金属学报,2006(03):321-324. |
| [4] | B. Zuo;N. Saraswati;T. Sritharan;H.H. Hng .Production and annealing of nanocrystalline Fe-Si and Fe-Si-Al alloy powders[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):210-216. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%