以钛酸丁酯为ＴｉＯ２前驱体，使ＴｉＯ２均匀分散于纯硅介孔分子筛ＭＣＭ－４１的介孔孔道内表面，利用ＴｉＯ２光学性质将ＡｕＣｌ－４还原为Ａｕ（０）并组装于氧化钛修饰的ＭＣＭ－４１孔道中．对所合成的Ａｕ负载的氧化钛修饰的ＭＣＭ－４１进行了ＸＲＤ，ＸＰＳ，Ｎ２吸附－脱附曲线，及固体ＵＶ－Ｖｉｓ漫反射等多种结构表征．由ＸＰＳ谱和固体ＵＶ－Ｖｉｓ漫反射吸收光谱的ｐｌａｓｍｏｎ吸收峰证明Ａｕ团簇呈现０价的金属状态．
Titania modified mesoporous slilcate MCM-41 (MCM-TiO2) was synthesized by precursor tetrabutyltitanate
and calcined MCM-41. Au clusters deposited on the inner surface of titania-modified MCM-41 by the photodeposition method through AuCl-4 and
MCM-TiO2 reaction. The structure and optical properties of the as-synthesized samples were investigated by XRD, XPS, N2 adsorption/
desorption isotherms and diffuse reflectance UV-Vis absorbance spectroscopy. The decrease of BET surface areas and the pore volume proved that nanosized
Au clusters deposited in the mesopore of MCM-TiO2. The Au 4f of XPS and the plasmon absorption in UV-Vis spectrum showed that the deposited Au was
in metal state.
参考文献
| [1] | Kresge C T, Leonowicz M E, Roth W J, et al. Nature, 1992, 359: 710--712. [2] Beck J S, Vartuli J C, Roth W J, et al. J. Am. Chem. Soc., 1992, 114: 10834--10843. [3] Moller K, Bein T. Chem. Mater., 1998, 10: 2950--2962. [4] 龙英才, 许太明, 孙尧俊, 等. 化学学报, 1999, 57: 1014--1021. [5] Abe T, Tachibana Y, Uematsu T, et al. Chem. Commun., 1995. 1617--1618. [6] Leon R, Margolese D, Stucky G, et al. Phys. Rev. B: Condens. Matter, 1995, 52: r2285--r2287. [7] O’Brien S, Keates J M, Barlow S, et al. Chem. Mater., 1998, 10: 4088--4099. [8] Kasuga T, Hiramatsu M, Hirano M, et al, J. Mater. Res., 1997, 12: 607--609. [9] Malato S, Blanco J, Richter C, et al. Appl. Catal. B: Environ., 1998, 17: 347--356. [10] Corma A, Martníez A, Martínez-Soria V. J. Catal., 1997, 169: 480--489. [11] Valden M, Lai X, Goodman D X. Science, 1998, 281: 1647--1650. [12] Zheng S, Gao L, Zhang Q, et al. J. Mater. Chem., 2000, 12: 723--727. [13] Luo K, St. Clair T P, Lai X, et al. J. Phys. Chem. B, 2000, 104: 3050--3057. [14] Zhao G, Kozuma H, Yoko T. Thin. Solid. Film, 1996, 277: 147--154. [15] Brust M, Walker M, Bethell D, et al. J. Chem. Soc., Chem. Commun., 1994. 801--802. |