分析了武钢生产的WGJ510C2钢在青岛、琼海和江津3个大气暴露试验点，暴露5a的腐蚀数据．结果表明，WGJ510C2钢的耐蚀性均优于Q345钢，两者的相对耐蚀性在青岛站是150％，住江津站是116％、在琼海站是146％．大气暴露5a带锈样的极化曲线测试结果表明，WGJ510C2钢的致钝电流、维钝电流均比对比钢Q345小，说明其锈层致密，防护性能好．
Five years atmospheric corrosion data collected from three exposure sites at Qingdao, Jiangjin and Qionghai of WISCO made WGJ510C2 steel were analyzed. The results indicate the corrosion resistance of WGJ510C2 is better than Q345 and the relative corrosion resistance for the two steels is 150%, 116% and 146% at Qingdao, Jiangjin and Qionghai respectively. The polarization curves of 5 year exposed rusty steel show that both the initial passivation current and the maintaining passivation current of WGJ510C2 are smaller than that of Q345, which indicates the better protective performance of WGJ510C2 may be due to its more compact rust layer.
参考文献
| [1] | 刘继雄,王青峰,李平和等.高性能耐火耐候建筑用钢焊接性能研究[J].钢铁,2002,37(12):40. |
| [2] | 陈晓,刘继雄,董汉雄等.高性能耐火耐候建筑用钢力学性能研究[J].钢结构,2002,17(3):39. |
| [3] | 刘继雄,李平和,王玉涛等.高性能耐火耐候建筑用钢自动埋弧焊焊评试验中的裂纹分析[J].焊接学报,2003,24(6):89. |
| [4] | 刘建容,张万灵,刘正生.锰对钢材耐大气腐蚀性的影响[J].钢铁研究,2010,(4):13. |
| [5] | 韩薇,汪俊,王振尧等.低合金钢耐大气腐蚀规律研究[J].腐蚀科学与防护技术,2003,15(6):315. |
| [6] | 严谨,熊长青.含铜低合金钢耐大气腐蚀性能研究一十五年大气暴露试验总结[J].中国腐蚀与防护学报,1986,6(1):1. |
| [7] | 刘建容,刘正生,张万灵.低合金钢大气腐蚀锈层的研究[J].工业建筑,2001,31:34. |
| [8] | 刘建容,张万灵.低合金钢的大气腐蚀规律研究[J].材料保护,2005,3s(10):18. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%