采用金相显微镜、扫描电镜及材料拉伸试验机等研究了异步轧制工艺制备的钢/铝复合板的组织与性能,探讨了异步速比对复合板界面剪切强度的影响.结果表明,异步轧制工艺可在30%的临界压下率下实现钢/铝的有效初结合,板材的初结合强度高于同步轧制样品.复合板的界面剪切强度随异步速比的增加先增大后减小,最佳的异步速比为1.2～1.25.异步轧制过程可实现钢基体粗大柱状晶的破碎与晶粒细化,轧后的复合板在450℃退火1h后即可以使钢基体获得理想的软化效果,克服了同步轧制样品在温度超过500℃退火时界面易生成脆性金属间化合物的难题.复合板的反复弯曲次数可达10次.
参考文献
| [1] | 李尧;崔建忠;马龙翔 .[J].钢铁,1990,4:42. |
| [2] | Jiang Z Y;Zhu H T;Tieu A K .[J].Key Engineering Materials,2004,274-276:718. |
| [3] | Kawaek A .[J].J Mater PR,2004,157-158:534. |
| [4] | Wauthier A;Regle H;Formigoni J et al.[J].Materials Characterization,2009,60:93. |
| [5] | Kim W J;Lee J B;Kim W Y et al.[J].Scripta Materialia,2007,56:310. |
| [6] | Huang M N;Pan S C;Tzou G Y et al.[J].J Mater PR,2006,177:117. |
| [7] | Salimi M;Kadkhodaei M .[J].J Mater PR,2004,150:215-222. |
| [8] | Nakaura Y;Watanabe A;Ohori K .[J].J Jpn Metas,2007,57:71. |
| [9] | Rydz D .[J].J Mater PR,2004,157-158:610. |
| [10] | Roumina R;Sinclair C W .[J].Met Mat TA,2008,39:2499. |
| [11] | Jindal V;Srivastava V C;Ghosh R N .[J].Mater Sci T,2008,24:801. |
| [12] | Chen Y L;Shan A D;Jiang J H et al.[J].Mater Sci F,2008,584-586:330. |
| [13] | Roumina R;Sinclair C W .[J].Met Mat T A,2008,39:2501. |
| [14] | 李立新;郑红专;王铭宗 等.[J].武汉钢铁学院学报(自然科学版),1994,17:36. |
| [15] | 林大超;史庆南;贺艳苓 等.[J].昆明理工大学学报,1997,22:81. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%