本研究采用CVI方法制备出了以Si-C-N陶瓷为基体以热解碳为界面的碳纤维增强陶瓷基复合材料(C/PyC/Si-C-N).用热膨胀仪和激光导热仪分别测试了C/PyC/Si-C-N的热膨胀性能和热扩散性能.研究结果表明:在25～1200℃范围内,C/PyC/Si-C-N复合材料的平均热膨胀系数为0.638×106 K-1;而热扩散率则随温度的升高而减小,并与温度呈一种指数关系,常温下的热扩散率约为0.00925 cm2·s-1.
参考文献
| [1] | Li-Anne Liew;Wenge Zhang;Victor M. Bright;Linan An;Martin L. Dunn;Rishi Raj.Fabrication of SiCN ceramic MEMS using injectable polymer-precursor technique[J].Sensors and Actuators, A. Physical,20011/2(1/2):64-70. |
| [2] | Rishi Raj;Linan An;Sandeep Shah.Oxidation Kinetics of an Amorphous Silicon Carbonitride Ceramic[J].Journal of the American Ceramic Society,20018(8):1803-1810. |
| [3] | 卢国锋;乔生儒;张程煜;侯军涛.碳纤维增强Si-C-N陶瓷基复合材料的氧化行为[J].硅酸盐学报,2008(11):1570-1576. |
| [4] | C. Pradere;C. Sauder.Transverse and longitudinal coefficient of thermal expansion of carbon fibers at high temperatures (300-2500 K)[J].Carbon: An International Journal Sponsored by the American Carbon Society,200814(14):1874-1884. |
| [5] | Xu Y;Zhang L;Ying H;Zhou W;Cheng L.Oxidation behavior and mechanical properties of C/SiC composites with Si-MoSi sub 2 oxidation protection coating[J].Journal of Materials Science,199924(24):6009-6014. |
| [6] | Fei WD;Wang LD.Thermal expansion behavior and thermal mismatch stress of aluminum matrix composite reinforced by beta-eucryptite particle and aluminum borate whisker[J].Materials Chemistry and Physics,20042/3(2/3):450-457. |
| [7] | Suresh Kumar;Anil Kumar;Anupam Shukla.Thermal-diffusivity measurement of 3D-stitched C-SiC composites[J].Journal of the European Ceramic Society,20093(3):489-495. |
| [8] | Laifei Cheng;Yongdong Xu;Qing Zhang;Litong Zhang.Thermal diffusivity of 3D C/SiC composites from room temperature to 1400 deg C[J].Carbon: An International Journal Sponsored by the American Carbon Society,20034(4):707-711. |
| [9] | Jie Chen;Yiguang Wang;Laifei Cheng.Thermal diffusivity of three-dimensional needled C/SiC-TaC composites[J].CERAMICS INTERNATIONAL,20118(8):3095-3099. |
| [10] | G. Amirthan;A. Udaya kumar;M. Balasubramanian.Thermal conductivity studies on Si/SiC ceramic composites[J].CERAMICS INTERNATIONAL,20111(1):423-426. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%