为研究硅对烧结高速钢力学性能的影响,采用真空热处理炉在1230℃对含0.4%碳粉及硅添加量在0～3.0%的M3:2高速钢进行烧结,在500～600℃对烧结后的试样进行二次回火.采用X射线衍射仪,扫描电镜及能谱分析等手段研究了不同硅添加量对回火态高速钢的物相特征及力学性能的影响规律.物相分析结果表明,添加硅后,硅主要分布在回火马氏体及M_6C碳化物中,而在MC碳化物中含量较低.回火马氏体组织中硅的含量随硅添加量的增加而增加,同时,硅的添加还显著影响回火马氏体组织中铁素体相的晶格常数,在硅添加量为0.7%时,铁素体相达到最大的晶格常数.力学性能测试结果表明,适量硅的添加可提高二次硬化效果,添加0.7%硅的高速钢在550 ℃二次回火后获得了最佳的硬度和弯曲强度.
To investigate the improvement of mechanical properties of high-speed steel by silicon addition,M3:2 high-speed steel with carbon addition of 0.4 wt.%and silicon addition in the range of 0～3.0 wt.%was sintered at 1230℃ using vacuum heat treatment furnace.and then followed by double tempering between 500℃ and 600℃.Effects of silicon addition on phase characteristics and mechanical properties of tempered M3:2 high-speed steel were investigated by using X-ray diffraction,scanning electron microscopy,and energy spectrum analysis.Phase analysis results show that silicon distributes mainly in tempered martensite and M_6C carbides,but rarely in MC carbides.The content of silicon in tempered martensite of high-speed steel increases with the increasing silicon addition.The addition of silicon exerts a crucial role on the the lattice constant of ferrite in tempered martensite.For the case of 0.7 wt.%silicon addition.the alloy exhibits the maximum lattice constant.Mechanical property test results show that suitable silicon addition Can improve the secondary hardening effects of M3:2 high-speed steel.M3:2 high-speed steel with 0.7 wt.%silicon addition possesses the excellent combination of high hardness and high bending strength after double tempering at 550℃.
参考文献
| [1] | 高家诚,胡金柱,王勇,李庆安,王平.粉末高速钢超固相线烧结制备耐磨摇臂镶块[J].材料科学与工艺,2008(04):495-497,501. |
| [2] | 范明月,刘和平,陶风强.采用粉末冶金技术提高工矿机械行业效益[J].山西机械,2001(01):3-5. |
| [3] | 郭庚辰.烧结高速钢的研究和发展动向[J].粉末冶金技术,2001(04):233-237. |
| [4] | 黄树涛,贾春德,姜增辉,于骏一.TiN涂层刀具高速车铣切削性能及磨损机理[J].哈尔滨工业大学学报,2008(09):1501-1505. |
| [5] | J.A. Jimenez;M. Carsi;G. Frommeyer .Microstructural and mechanical characterisation of composite materials consisting of M3/2 high speed steel reinforced with niobium carbides[J].Powder Metallurgy,2005(4):371-376. |
| [6] | Leszek A. Dobrzanski;Adam Zarychta .The structure and properties of W-Mo-V high-speed steels with increased contents of Si and Nb after heat treatment[J].Journal of Materials Processing Technology,1998(1/3):180-193. |
| [7] | L. A. Dobrzanski;M. Adamiak;A. Zarychta .The structure and properties of heat-treated and coated W-Mo-V+Si+Nb high-speed steels[J].Journal of Materials Processing Technology,1999(0):520-527. |
| [8] | Fusheng Pan;Peidao Ding;Shouze Zhou .Effects of silicon additions on the mechanical properties and microstructure of high speed steels[J].Acta materialia,1997(11):4703-4712. |
| [9] | W. Khraisat;L. Nyborg;P. Sotkovszki .Effect of silicon, vanadium and nickel on microstructure of liquid phase sintered M3/2 grade high speed steel[J].Powder Metallurgy,2005(1):33-38. |
| [10] | Fusheng Pan;Mtsuji Hirohashi;Yun Lu .Carbides in High-speed Steels Containing Silicon[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2004(9):2757-2766. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%