为克服2024铝合金表面单独钒盐或锆盐转化膜存在裂纹而导致其耐蚀性能不佳的问题,采用由氟锆酸钾、偏钒酸钠组成的转化液,在2024铝合金表面制备了钒锆复合转化膜.采用扫描电镜、能谱仪分析了复合膜的形貌及成分,采用中性盐雾试验和极化曲线研究了其耐蚀性能,采用百格法划格法研究了复合膜与基体的结合力及复合膜与漆膜的结合力.采用单因素法对转化液组分及转化条件进行了优选.结果表明:在2.0 g/L K2ZrF6,2.5 g/L NaVO3组成的转化液中,在pH值为3.0,温度为65℃的条件下反应20 min,所得钒锆复合膜致密、无裂纹,由O,F,Mg,Al,Zr,V,Cu等元素组成,膜基、膜漆结合较好,复合膜腐蚀电位较基体正移了86 mV,腐蚀电流密度减小为基材的1/5,耐蚀性能较基体明显提高.
参考文献
| [1] | 张圣麟.铝合金表面处理技术[M].北京:化学工业出版社,2009:5-65. |
| [2] | Campestrini P.;Terryn H.;Hovestad A.;de Wit JHW. .Formation of a cerium-based conversion coating on AA2024: relationship with the microstructure[J].Surface & Coatings Technology,2004(3):365-381. |
| [3] | Hongwei Shi;En-Hou Han;Fuchun Liu;Silvar Kallip .Protection of 2024-T3 aluminium alloy by corrosion resistant phytic acid conversion coating[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Sep.1):325-331. |
| [4] | F.O. George;P. Skeldon;G.E. Thompson .Formation of zirconium-based conversion coatings on aluminium and Al-Cu alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Dec.):231-237. |
| [5] | 张学颖,薛丽华,吕坤,王永光,张建旗.铝合金2024上钒酸盐转化膜的研究[J].内蒙古科技大学学报,2010(04):327-329,333. |
| [6] | 周绮;张春丽;张广森 .铝合金锫酸盐化学转化膜的制备[J].腐蚀与防护,2010,31(02):158-160. |
| [7] | 郭瑞光,耿志良.无铬转化膜技术研究的几点建议[J].电镀与涂饰,2008(05):38-40. |
| [8] | 杨绍利;陈厚生.钒钛材料[M].北京:冶金工业出版社,2007:28-29. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%