采用热分解法制备了非贵金属SnO2+Sb2O4中间层Ti基MO2活性层电极,利用SEM,XRD和XPS方法对中间层进行了表征.测定了Ti/SnO2+Sb2O4/MnO2和Ti/SnO2+Sb2O4/PbO2电极在硫酸溶液中的析氧极化曲线,二者起始析氧过电位均比贵金属小;考察了在高电流密度(4A/cm2)下的加速寿命,二者依次分别达到18 h和86 h.实验表明,SnO2+Sb2O4是一种具有良好导电性和结合力的耐酸Ti基MO2电极中间层材料.
参考文献
| [1] | Terezo A J;Pereira E C .[J].Electrochimica Acta,2000,45(25-26):4351. |
| [2] | Park Tae Joo;Jeong Doo Seok;Hwang Cheol Seong et al.[J].Thin Solid Films,2005,471(1-2):236. |
| [3] | Terezo Ailton J;Pereira Ernesto C .[J].Materials Letters,2002,53(4-5):339. |
| [4] | Mahé Eric;Devilliers Didier .[J].Electrochimica Acta,2001,46(05):629. |
| [5] | Cao Dianxue;Bergens Steven H .[J].Journal of Power Sources,2004,134(02):170. |
| [6] | Nijjer S;Thonstad J;Haarberg G M .[J].Electrochimica Acta,2000,46(2-3):395. |
| [7] | LIANG Zhen-hai;FAN Cai-mei;SUN Yan-ping .Electrocatalysis of Oxygen Evolution Reaction on Ti/SnO_2+RuO_2+MnO_2/MnO_2 W\Electrode in Sulfuric Acid Solution[J].Chemical Research in Chinese Universities,2001(3):287-292. |
| [8] | Chen Xueming;Chen Guohua .[J].Electrochimica Acta,2005,50(20):4155. |
| [9] | Chiaki Iwakura;Meguru Inai;Masatsugu Manabe .[J].电化学すよひ工业物理化学,1980,48(02):91. |
| [10] | 罗文秀;任鹏程;谭忠恪 .[J].功能材料,1993,24(02):129. |
| [11] | 刘世宏;王当憨;潘承璜.X射线光电子能谱分析[M].北京:科学出版社,1988:313. |
| [12] | 王静,冯玉杰.制备方法对稀土Gd掺杂SnO2/Sb电催化电极性能的影响[J].吉林大学学报（理学版）,2005(04):546-550. |
| [13] | 曹晓平;姚文清;叶小燕 et al.[J].化学物理学报,1997,10(03):255. |
| [14] | 荀欣;张惠良 .[J].化学研究与应用,1998,10(02):159. |
| [15] | Miles M H;Klaus E A;Gunn B P et al.[J].Electrochimica Acta,1978,23:521. |
| [16] | 曾人杰.无机材料化学[M].厦门:厦门大学出版社,2001:187. |
| [17] | 杨建广;唐谟堂;唐朝波 et al.[J].纳米材料与结构,2004,4:18. |
| [18] | 刘杏芹,朱海宁,沈瑜生.SbxSn1-xO2固溶体系电学性能与导电机制研究[J].无机化学学报,1996(02):130-134. |
| [19] | Kotz R;Stucki S;Carcer B .[J].Journal of Applied Electrochemistry,1991,21(01):14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%